RESUMO
OBJECTIVE: To evaluate the ability of casein phosphopeptide/amorphous calcium phosphate (CPP/ACP) and lysozyme, lactoferrin, and lactoperoxidase (LLL) added to glass ionomer cement (GIC) to inhibit the growth of S. mutans in a caries model. MATERIAL AND METHODS: Eighty permanent third molars were selected. The dentin of these teeth was exposed and flattened. Except for the coronal dentin, the specimens were waterproofed, autoclaved, and submitted to cariogenic challenge with standard strain of S. mutans. The carious lesions were sealed as follows: group 1 (n=20): GIC without additives; group 2 (n=20): GIC + CPP/ACP; group 3 (n=20): GIC + LLL; group 4 (n=20): GIC + CPP/ACP + LLL. S. mutans counts were performed before the caries were sealed (n=5), after 24 hours (n=5), at 1 month (n=5), and at 6 months (n=5). The results were analyzed using descriptive statistical analysis and the Kruskal-Wallis test (Student-Newman-Keuls test). RESULTS: GIC + LLL caused a significant reduction of S. mutans 1 month after sealing (p<0.01); however, there was a significant growth of S. mutans 6 months after sealing. GIC, GIC + CPP/ACP, and GIC + CPP/ACP + LLL showed similar behavior with significant reduction of S. mutans after 24 hours (p<0.05) and increase after 1 and 6 months. CONCLUSION: The addition of LLL to GIC increases the antimicrobial action of GIC on S. mutans. This leads to control of bacterial biofilm for 1 month, thus stopping the progression of carious lesions.
RESUMO
AIM: To assess the influence of dentin substrate and chlorhexidine on the marginal seal of composite resin restorations. MATERIALS AND METHODS: The sample comprised 20 third molars. Four cavities were drilled in the dentin sur face, followed by sealing and restoration of sound dentin (n = 10) or carious dentin (n = 10). In the control group, cavities were immediately restored as follows: G1: one-bottle bonding agent (OB) + composite resin (CR); G2: chlorhexidine 2.0% (CLX) + OB + CR; G3: self-etch bonding agent (SE) + CR; G4: CLX + SE + CR. In the experimental group (carious dentin), carious lesions were induced with S. mutans and cavities were restored as in the control group. Five specimens from each group (sound and carious) were stored in brain-heart infusion (BHI) medium for 6 months. All specimens were submerged in methylene blue 0.5% to test for microleakage. The Kruskal-Wallis and Student-Newman-Keuls tests were used to assess results. RESULTS: On immediate assessment, there were no significant between-group differences in the sound dentin group, whereas in carious dentin, there was less leakage when OB and CLX were used. At 6 months, there was less leakage in the sound dentin group when OB and CLX were used; there were no between-group differences in carious dentin. Comparison of immediate and 6-month assessments showed a significant increase in leakage at 6 months when sound dentin was treated with SE and CLX and when carious dentin was treated with OB and CLX. CONCLUSION: To ensure better dentin hybridization and preservation of the organic constituents of the dentin matrix, the properties of chlorhexidine digluconate and the components of the resin matrix must be taken into account. CLINICAL SIGNIFICANCE: Metalloproteinases influence degradation of the hybrid layer in composite resin restorations, regardless of whether the bonding system used is one-bottle or self-etching.