Phys Chem Chem Phys ; 24(25): 15428-15438, 2022 Jun 29.
Artigo em Inglês | MEDLINE | ID: mdl-35708199

RESUMO

LEV type zeolites were synthesized with four different structure-directing agents and converted to copper loaded NH3-SCR catalysts. The synthesis recipe was found to impact the respective Al population in the two topologically different framework sites in double and single 6-rings, resolvable by 27Al MAS NMR spectroscopy. Hydrothermal stability was found to be related to the silanol concentration, Si/Al ratio, particle size, crystal morphology, crystal defects, external surface area, and microporosity. Catalytic activity in NH3-SCR was dependent on preferential Al siting in the double 6-rings. Levinite synthesized using adamantylamine showed the strongest preference for Al atoms sitting in double 6-ring sites, and showed the highest catalytic turnover frequency. Unfortunately, because of the large crystal size, copper loading of this sample was limited to 0.6 wt% while other samples could be loaded with copper up to 3.3 wt%. An optimum combination of hydrothermal stability and catalytic activity was obtained with N,N'-bis-dimethylpentanediyldiammonium dibromide as structure-directing agent.

2.
Nanoscale Adv ; 1(8): 2873-2880, 2019 Aug 06.
Artigo em Inglês | MEDLINE | ID: mdl-36133590

RESUMO

Carbon black is chemically modified by selective photocatalytic oxidation, removing amorphous carbon and functionalizing the graphitic fraction to produce porous, graphitized carbon black, commonly used as an adsorbent in chromatography. In contrast to pyrolytic treatments, this photocatalytic modification proceeds under mild reaction conditions using oxygen, nitric oxide, water vapor and a titanium dioxide photocatalyst at 150 °C. The photo-oxidation can be performed both with the photocatalyst in close proximity (contact mode) or physically separated from the carbon. Structural analysis of remotely photo-oxidized carbon black reveals increased hydrophilic properties as compared to pyrolysis at 700 °C in a N2 atmosphere. Carbon black photo-oxidation selectively mineralizes sp3-hybridized carbon, leading to enhanced graphitization. This results in an overall improved structural ordering by enriching carbon black with sp2-hybridized graphitic carbon showing decreased interplanar distance, accompanied by a twofold increase in the specific surface area. In addition, the photo-oxidized material is activated by the presence of oxygen functionalities on the graphitic carbon fraction, further enhancing the adsorptive properties.

3.
Chem Commun (Camb) ; 54(44): 5626-5629, 2018 May 29.
Artigo em Inglês | MEDLINE | ID: mdl-29770814

RESUMO

EU-7 zeolite with Si/Al ratio of 15 is identified as a BIK type zeolite. The framework charge is compensated with Cs+ cations located in 8-ring channels at regular distances. Even partially exchanged, Cu-loaded EU-7 is active in NH3-SCR and withstands hydrothermal aging at 900 °C needed for application in diesel particulate filters.

4.
Phys Chem Chem Phys ; 18(28): 18795-801, 2016 Jul 28.
Artigo em Inglês | MEDLINE | ID: mdl-27346703

RESUMO

-COK-14 zeolite, the variant of COK-14 (OKO topology) with a systematically interrupted framework, exhibits unusual behaviour in high pressure intrusion-extrusion cycles of 20 M LiCl solution. After the first cycle with deviating behaviour and partially irreversible intrusion, subsequent cycles show stable reversible behaviour. The system behaves like a spring with unique progressive intrusion in the range of 10-120 MPa followed by enhanced uptake before saturation. While the intrusion-extrusion cycling leads to fragmented crystals, powder diffraction reveals high crystallinity of the fragments. Based on the detailed characterisation of the zeolite samples with XRD, Rietveld refinement, N2 adsorption, TGA and (29)Si MAS NMR before and after intrusion-extrusion experiments, a model of the structure of the intruded -COK-14 samples is proposed. Intrusion-extrusion of LiCl solution systematically breaks the most strained bonds in the structure which results in a new framework connectivity with enhanced stability, which persists during the harsh intrusion-extrusion conditions.