Cartilage regeneration with dual-drug-releasing injectable hydrogel/microparticle system: In vitro and in vivo study.

In this study, we developed an injectable in situ forming hydrogel/microparticle system consisting of two drugs, melatonin and methylprednisolone, to investigate the capability of the system for chondrogenesis in vitro and in vivo. The chemical, mechanical, and rheological properties of the hydrogel/microparticle were investigated. For in vitro evaluation, the adipose-derived stem cells might be mixed with hydrogel/microparticles, then cellular viability was analyzed by acridine orange/propidium iodide and 4',6-diamidino-2-phenylindole staining and also dimethylmethylene blue assay were conducted to find the amount of proteoglycan. The real-time polymerase chain reaction for aggrecan, sex-determining region Y-Box 9, collagen I (COL1), and COL2 gene expression was performed after 14 and 21 days. For evaluation of cartilage regeneration, the samples were implanted in rabbit knees with cartilaginous experimental defects. Defects were created in both knees of three groups of rabbits. Group 1 was the control with no injection, and Groups 2 and 3 were loaded with hydrogel/cell and hydrogel/microparticle/cell; respectively. Then, after 3 and 6 months, histological evaluations of the defected sites were carried out. The amount of glycosaminoglycans after 14 and 21 days increased significantly in hydrogels/microparticles loaded with cells. The expression of marker genes was also significant in hydrogels/microparticles loaded with cells. According to histology analysis, the hydrogels/microparticles loaded with cells showed the best cartilage regeneration. Overall, our study revealed that the developed injectable hydrogel/microparticle can be used for cartilage regeneration.

Bone marrow or adipose tissue mesenchymal stem cells: Comparison of the therapeutic potentials in mice model of acute liver failure.

Acute liver failure (ALF) is a lethal disease with limited life-saving therapy. Because lack of whole organ donors for liver transplantation, a substitute treatment strategy is needed for these patients. Preclinical and clinical findings have proved that treatment with mesenchymal stem cells (MSCs) is beneficial for recovery from ALF. In this approach, however, the appropriate sources of these cells are unclear. In the present study, we investigated and compared the therapeutic potentials of bone marrow-mesenchymal stem cells (BM-MSC) with those of adipose tissue (AT-MSC) in carbon tetrachloride (CCL4)-induced acute liver failure in mice. Murine BM- and AT-MSCs obtained from normal mice were cultured and labelled. The cells were transplanted to CCL4-induced ALF mice models intravenously. After cell transplantation, blood samples and liver tissues were collected daily for 72 h to analyze liver enzymes and liver histopathology, respectively. We found that survival rate of AT-MSC transplanted (AT-TR) mice was significantly higher than that of control (ALF) group. Liver histopathology was superior in the AT-TR mice, but not significantly, compared to that in BM-MSC transplanted (BM-TR) ones. Furthermore, in the AT-TR mice the level of aspartate aminotransferase (AST) and alanine aminotransferase (ALT), in some time points were significantly less than those of BM-TR. Taken together, these data suggest that in comparison to BM-MSC, AT-MSCs is an appropriate choice for cell therapy in the case of acute liver failure.

Bladder smooth muscle cells on electrospun poly(ε-caprolactone)/poly(l-lactic acid) scaffold promote bladder regeneration in a canine model.

Engineering of urinary bladder has been the focus of numerous studies in recent decade. Novel biomaterials, innovative fabrication methods and various modification processes of scaffolds are the critical issues to find supportive matrices. Supportive characteristics of electrospun PCL/PLLA nano-scaffold for bladder augmentation in canine model and the role of bladder cells in regeneration process were appraised. Electrospun PCL/PLLA was fabricated by co-electrospinning of PCL and PLLA. Bladder cells were isolated and transduced with lentiviral particles encoding eGFP and JRed proteins. Electrospun PCL/PLLA was seeded with different bladder cells individually or in co-culture condition. Cell-free and cell-seeded electrospun PCL/PLLA scaffolds (10cm2) were surgically implanted in bladders of eight female dogs for three months. To evaluate bladder regeneration, the dogs were sacrificed and their bladders were examined macroscopically and microscopically for presence of tracking proteins, expression of cell-specific markers and histological attributes of regenerated tissues. All animals survived the experiment with no complication. In smooth muscle transplanted group complete regeneration and covering of scaffold were observed. Other groups revealed partial regeneration. A well-developed layer of urothelium was formed in all groups in regenerated parts. Smooth muscle transplanted group showed the most developed muscle layer. Regenerated tissue demonstrated typical expression of cell-specific markers. No expression of eGFP and JRed was observed. Electrospun PCL/PLLA scaffold with proper handling, suture retention, nano-sized surface features, maintenance of normal phenotype of cells and minimal adverse effects in body can be a supportive substrate for bladder wall regeneration when seeded with bladder smooth muscle cells.

Regeneration of meniscus tissue using adipose mesenchymal stem cells-chondrocytes co-culture on a hybrid scaffold: In vivo study.

The meniscus has poor intrinsic regenerative capacity and its damage inevitably leads to articular cartilage degeneration. We focused on evaluating the effects of Polyvinyl alcohol/Chitosan (PVA/Ch) scaffold seeded by adipose-derived mesenchymal stem cell (ASC) and articular chondrocytes (AC) in meniscus regeneration. The PVA/Ch scaffolds with different molar contents of Ch (Ch1, Ch2, Ch4 and Ch8) were cross-linked by pre-polyurethane chains. By increasing amount of Ch tensile modulus was increased from 83.51 MPa for Ch1 to 110 MPa for Ch8 while toughness showed decrease from 0.33 mJ/mm3 in Ch1 to 0.11 mJ/mm3 in Ch8 constructs. Moreover, swelling ratio and degradation rate increased with an increase in Ch amount. Scanning electron microscopy imaging was performed for pore size measurement and cell attachment. At day 21, Ch4 construct seeded by AC showed the highest expression with 24.3 and 22.64 folds increase in collagen II and aggrecan (p ≤ 0.05), respectively. Since, the mechanical properties, water uptake and degradation rate of Ch4 and Ch8 compositions had no statistically significant differences, Ch4 was selected for in vivo study. New Zealand rabbits were underwent unilateral total medial meniscectomy and AC/scaffold, ASC/scaffold, AC-ASC (co-culture)/scaffold and cell-free scaffold were engrafted. At 7 months post-implantation, macroscopic, histologic, and immunofluorescent studies for regenerated meniscus revealed better results in AC/scaffold group followed by AC-ASC/scaffold and ASC/scaffold groups. In the cell-free scaffold group, there was no obvious meniscus regeneration. Articular cartilages were best preserved in AC/scaffold group. The best histological score was observed in AC/scaffold group. Our results support that Ch4 scaffold seeded by AC alone can successfully regenerate meniscus in tearing injury and ASC has no significant contribution in the healing process.