Novel Approach to Landfill Wastewater Treatment Fouling Mitigation: Air Gap Membrane Distillation with Tin Sulfide-Coated PTFE Membrane.

This study addressed the fouling issue in membrane distillation (M.D.) technology, a promising method for water purification and wastewater reclamation. To enhance the anti-fouling properties of the M.D. membrane, a tin sulfide (TS) coating onto polytetrafluoroethylene (PTFE) was proposed and evaluated with air gap membrane distillation (AGMD) using landfill leachate wastewater at high recovery rates (80% and 90%). The presence of TS on the membrane surface was confirmed using various techniques, such as Field Emission Scanning Electron Microscopy (FE-SEM), Fourier Transform Infrared Spectroscopy (FT-IR), Energy Dispersive Spectroscopy (EDS), contact angle measurement, and porosity analysis. The results indicated the TS-PTFE membrane exhibited better anti-fouling properties than the pristine PTFE membrane, and its fouling factors (FFs) were 10.4-13.1% compared to 14.4-16.5% for the PTFE membrane. The fouling was attributed to pore blockage and cake formation of carbonous and nitrogenous compounds. The study also found that physical cleaning with deionized (DI) water effectively restored the water flux, with more than 97% recovered for the TS-PTFE membrane. Additionally, the TS-PTFE membrane showed better water flux and product quality at 55 °C and excellent stability in maintaining the contact angle over time compared to the PTFE membrane.

Application of lamellar nickel hydroxide membrane as a tunable platform for ionic thermoelectric studies.

The recent trend in thermoelectric literature suggests that ionic thermoelectric (i-TE) materials are ideal for directly converting low-grade waste heat into electricity. Here, we developed a unique platform for i-TE studies by stacking two-dimensional sheets of ß-Ni(OH)2 prepared by a bottom-up method. The lamellar membrane of ß-Ni(OH)2 (Ni-M) itself does not display significant thermovoltages, but when doped with mobile anion-generating species (like aminopropyl functionalized magnesium phyllosilicate or organic halide salts), it exhibits significant negative Seebeck coefficient (up to -13.7 ± 0.2 mV K-1). Similarly, upon doping with cation-generating species like poly(4-styrene sulfonic acid) (PSS), it displays positive Seebeck coefficient values (up to +12 ± 1.9 mV K-1). The positive and negative i-TE materials prepared by doping Ni-M are assembled into ionic thermopiles capable of generating thermovoltages up to 1 V, at ΔT = 12 K. The Ni-M-based nanofluidic systems demonstrated an additional path of electricity harvesting by connecting colder zones of the positive and negative i-TE materials with other ion conducting membranes. In contrast to organic polymer-based i-TE systems, the Ni-M based system exhibited consistent performance despite being exposed to high temperatures (∼200 °C, 5 minutes).

Fouling and Performance Investigation of Membrane Distillation at Elevated Recoveries for Seawater Desalination and Wastewater Reclamation.

This study reports on the impact of elevated recovery (i.e., 80%, 85%, and 90%) on the fouling and performance of air gap membrane distillation (AGMD) with real seawater and landfill leachate wastewater samples using polytetrafluoroethylene (PTFE) polymer membranes. Increasing the feed temperature from 55 °C to 65 °C improved the water flux of seawater and wastewater and shortened the operating time by 42.8% for all recoveries. The average water flux in the 80%, 85%, and 90% recovery experiments at the 65 °C feed temperature was 32%, 37.32%, and 36.7% higher than the case of 55 °C for the same recoveries. The water flux decline was more severe at a higher temperature and recovery. The highest flux decline was observed with a 90% recovery at 65 °C feed temperature, followed by an 85% recovery at 65 °C. Close examination of the foulants layer revealed that seawater formed a cake fouling layer made predominantly of metal oxides. In contrast, the landfill leachate fouling was a combination of pore blocking and cake formation, consisting mainly of carbonous and nitrogenous compounds. Physical cleaning with deionized (DI) water at 55 °C and 65 °C and chemical cleaning with hydrogen peroxide (H2O2) were investigated for their efficiency in removing membrane foulants. Analytical results revealed that seawater fouling caused membrane pore blockage while wastewater fouling formed a porous layer on the membrane surface. The results showed that membrane cleaning with hydrogen peroxide restored >97% of the water flux. Interestingly, the fouling factor in seawater tests was 10%, while it was 16% for the wastewater tests.

Sodium docusate as a cleaning agent for forward osmosis membranes fouled by landfill leachate wastewater.

Membrane cleaning is critical for economic and scientific reasons in wastewater treatment systems. Sodium docusate is a laxative agent and removes cerumen (ear wax). Docusate penetrates the hard ear wax, making it softer and easier to remove. The same concept could be applied to soften and remove fouling layers on the membrane surface. Once softened, the foulants can be easily flushed with water. This innovative approach can address the challenge of developing superior methods to mitigate membrane fouling and material degradation. In this study, we evaluated the efficiency of sodium docusate for cleaning fouled forward osmosis membranes with real landfill leachate wastewater. Experiments were conducted to examine the impact of dose rate, contact time, flow or static conditions, and process configuration (forward osmosis (FO) or pressure retarded osmosis (PRO) upon fouling created by landfill leachate dewatering. A remarkable (99%) flux recovery was achieved using docusate at a small concentration of only 0.1% for 30 min. Furthermore, docusate can also effectively restore flux with static cleaning without using pumps to circulate the cleaning solution. Furthermore, cleaning efficiency can be achieved at neutral pH compatible with most membrane materials. From an economic and energy-saving perspective, static cleaning can almost achieve the same cleaning efficiency as kinetic cleaning for fouled forward osmosis membranes without the expense of additional pumping energy compared to kinetic cleaning. Since pumping energy is a major contributor to the overall energy of the forward osmosis system, it can be minimized to a certain degree by using a static cleaning approach and can bring good energy savings when using larger membrane areas. Studies of the contact angle on the membrane surface indicated that the contact angle was decreased compared to the fouled membrane after cleaning (e.g. 70.3° to 63.2° or FO mode and static cleaning). Scanning Electron Microscopy revealed that the cleaning strategy was successful. Infrared Spectroscopy showed that a small amount of sodium docusate remained on the membrane surface. Docusate is more environmentally friendly than acid or alkaline solutions from an environmental perspective. Furthermore, the cleaning solution can be reused for several cycles without discarding it due to the surfactant properties of docusate.