Reactive Vapor-Phase Inhibitors for Area-Selective Depositions at Tunable Critical Dimensions.

Area-selective depositions (ASD) take advantage of the chemical contrast between material surfaces in device fabrication, where a film can be selectively grown by chemical vapor deposition on metal versus a dielectric, for instance, and can provide a path to nontraditional device architectures as well as the potential to improve existing device fabrication schemes. While ASD can be accessed through a variety of methods, the incorporation of reactive moieties in inhibitors presents several advantages, such as increasing thermal stability and limiting precursor diffusion into the blocking layer. Alkyne-terminated small molecule inhibitors (SMIs)─propargyl, dipropargyl, and tripropargylamine─were evaluated as metal-selective inhibitors. Modeling these SMIs provided insight into the binding mechanism, influence of sterics, and complex polymer network formed from the reaction between inhibitors consisting of alkene, aromatic, and network branchpoints. While a significant contrast in the binding of the SMIs on copper versus a dielectric was observed, residual amounts were detected on the dielectric surfaces, leading to variable ALD growth rates dependent on pattern-critical dimensions. This behavior can be controlled and utilized to direct film growth on patterns only above a critical threshold dimension; below this threshold, both the dielectric and metal features are protected. This method provides another design parameter for ASD processes and may extend its application to broader-ranging device fabrication schemes.

Additive Lithography-Organic Monolayer Patterning Coupled with an Area-Selective Deposition.

The combination of area-selective deposition (ASD) with a patternable organic monolayer provides a versatile additive lithography platform, enabling the generation of a variety of nanoscale feature geometries. Stearate hydroxamic acid self-assembled monolayers (SAMs) were patterned with extreme ultraviolet (λ = 13.5 nm) or electron beam irradiation and developed with ASD to achieve line space patterns as small as 50 nm. Density functional theory was employed to aid in the synthesis of hydroxamic acid derivatives with optimized packing density to enhance the imaging contrast and improve dose sensitivity. Near-edge X-ray absorption fine structure spectroscopy and infrared spectroscopy reveal that the imaging mechanism is based on improved deposition inhibition provided by the cross-linking of the SAM to produce a more effective barrier during a subsequent deposition step. With patterned substrates composed of coplanar copper lines and silicon spacers, hydroxamic acids selectively formed monolayers on the metal portions and could undergo a pattern-wise exposure followed by ASD in the first combination of a patternable monolayer with ASD. This material system presents an additional capability compared to traditional ASD approaches that generally reflect a starting patterned surface. Furthermore, this bottoms-up additive approach to lithography may be a viable alternative to subtractive nanoscale feature generation.

Imaging thin films of nanoporous low-k dielectrics: comparison between ultramicrotomy and focused ion beam preparations for transmission electron microscopy.

Ultramicrotomy, the technique of cutting nanometers-thin slices of material using a diamond knife, was applied to prepare transmission electron microscope (TEM) specimens of nanoporous poly(methylsilsesquioxane) (PMSSQ) thin films. This technique was compared to focused ion beam (FIB) cross-section preparation to address possible artifacts resulting from deformation of nanoporous microstructure during the sample preparation. It was found that ultramicrotomy is a successful TEM specimen preparation method for nanoporous PMSSQ thin films when combined with low-energy ion milling as a final step. A thick, sacrificial carbon coating was identified as a method of reducing defects from the FIB process which included film shrinkage and pore deformation.