Effect of zircon-based tricolor pigments on the color, microstructure, flexural strength and translucency of a novel dental lithium disilicate glass-ceramic.

The purpose of this study was to investigate the effect of zircon-based tricolor pigments (praseodymium zircon yellow, ferrum zircon red, and vanadium zircon blue) on the color, thermal property, crystalline phase composition, microstructure, flexural strength, and translucency of a novel dental lithium disilicate glass-ceramic. The pigments were added to the glass frit, milled, pressed, and sintered. Ninety monochrome samples were prepared and the colors were analyzed. The effect of the pigments on thermal property, crystalline phase composition, and microstructure were determined by differential scanning calorimetry (DSC), X-ray diffraction (XRD), and scanning electron microscopy (SEM), respectively. Addition of the pigments resulted in the acquisition of subtractive primary colors as well as tooth-like colors, and did not demonstrate significant effects on the thermal property, crystalline phase composition, microstructure, and flexural strength of the experimental glass-ceramic. Although significant differences (p < 0.01) were observed between the translucencies of the uncolored and 1.0 wt % zircon-based pigment colored ceramics, the translucencies of the latter were sufficient to fabricate dental restorations. These results indicate that the zircon-based tricolor pigments can be used with dental lithium disilicate glass-ceramic to produce abundant and predictable tooth-like colors without significant adverse effects, if mixed in the right proportions.

Effects of local delivery of bFGF from PLGA microspheres on osseointegration around implants in diabetic rats.

OBJECTIVE: Diabetes mellitus may impair bone healing after dental implant placement. The objective of this study was to evaluate the effects of the local delivery of basic fibroblast growth factor (bFGF) from poly(lactide-co-glycolide) (PLGA) microspheres on osseointegration around titanium implants in diabetic rats. STUDY DESIGN: The bFGF-PLGA microspheres were prepared by the W/O/W double-emulsion solvent evaporation method. A total of 20 rats were used to create diabetic animal models by giving them a high-fat and high-sugar diet and a low-dose streptozotocin intraperitoneal injection. Titanium implants were planted into the tibias of the diabetic rats and into 10 normal rats. Microspheres were loaded on the surfaces of the implants in the bFGF intervention group before they were placed into the rats. After 4 or 8 weeks, the tibias containing the implants were removed and embedded with resin. Uncalcified tissue slices were prepared to compare osseointegration. RESULTS: At 4 weeks, the bone-implant contact rate in the diabetic control group was less than that in the control group and the bFGF intervention group (P < .05). At 8 weeks, the results among the 3 groups were similar to those at 4 weeks. CONCLUSIONS: The local delivery of bFGF from PLGA microspheres into areas around titanium implants may improve osseointegration in diabetic rats.