RESUMO
A novel hole-transporting molecule (F101) based on a furan core has been synthesized by means of a short, high-yielding route. When used as the hole-transporting material (HTM) in mesoporous methylammonium lead halide perovskite solar cells (PSCs) it produced better device performance than the current state-of-the-art HTM 2,2',7,7'-tetrakis-(N,N-di-p-methoxyphenylamine)-9,9'-spirobifluorene (spiro-OMeTAD). The F101-HTM-based device exhibited both slightly higher Jsc (19.63 vs. 18.41â mA cm(-2) ) and Voc (1.1 vs. 1.05â V) resulting in a marginally higher power conversion efficiency (PCE) (13.1 vs. 13 %). The steady-state and time-resolved photoluminescence show that F101 has significant charge extraction ability. The simple molecular structure, short synthesis route with high yield and better performance in devices makes F101 an excellent candidate for replacing the expensive spiro-OMeTAD as HTM in PSCs.
RESUMO
Lead-halide perovskites have transcended photovoltaics. Perovskite light-emitting diodes (PeLEDs) emerge as a new field to leverage on these fascinating semiconductors. Here, we report the first use of completely inorganic CsPbBr3 thin films for enhanced light emission through controlled modulation of the trap density by varying the CsBr-PbBr2 precursor concentration. Although pure CsPbBr3 films can be deposited from equimolar CsBr-PbBr2 and CsBr-rich solutions, strikingly narrow emission line (17 nm), accompanied by elongated radiative lifetimes (3.9 ns) and increased photoluminescence quantum yield (16%), was achieved with the latter. This is translated into the enhanced performance of the resulting PeLED devices, with lower turn-on voltage (3 V), narrow electroluminescence spectra (18 nm) and higher electroluminescence intensity (407 Cd/m(2)) achieved from the CsBr-rich solutions.