Influence of drying protocol with isopropyl alcohol on the bond strength of resin-based sealers to the root dentin.

INTRODUCTION: This study compared the bond strength, interfacial ultrastructure, and tag penetration of resin-based sealers applied to smear-free radicular dentin using 70% isopropyl alcohol as the active final rinse. METHODS: Eighty root canals were prepared and assigned to 2 groups (n = 40) according to the drying protocol: paper points or 70% isopropyl alcohol. Then, roots were divided into 4 subgroups (n = 10) with respect to the sealer and obturation material: AH Plus (Dentsply De Trey GmbH, Konstanz, Germany) and gutta-percha (AH/GP), Hybrid Root SEAL (Sun Medical, Tokyo, Japan) and gutta-percha (HR/GP), Epiphany SE (Pentron Clinical Technologies, Wallingford, CT) and gutta-percha (EP/GP), and Epiphany SE and Resilon (EP/RS). Roots were sectioned, and the push-out test was performed. Failure modes were examined under stereomicroscopy and sealer penetration into the dentinal tubules under scanning electron microscopy. Data were statistically analyzed by 2-way analysis of variance post hoc Tukey tests with a significant level of 5%. RESULTS: Overall, canals dried with isopropyl alcohol showed significantly higher bond strength values (2.11 ± 1.74 MPa) than with paper points (1.81 ± 1.73 MPa) (P < .05). The HR/GP group showed lower bond strength than the AH/GP group (P < .05) but higher than the EP/GP and EP/RS groups (P < .05). The most frequent type of failure was cohesive in the AH/GP and HR/GP groups and adhesive in the EP/GP and EP/RS groups. Scanning electron microscopic evaluation revealed better adaptation of the adhesive interface in the AH/GP and HR/GP groups in comparison with the EP/GP and EP/RS groups. CONCLUSIONS: A final rinse with EDTA and 70% isopropyl alcohol improved the bond strength and penetration of the sealers into dentinal tubules of the root.

Influence of finishing/polishing on color stability and surface roughness of composites submitted to accelerated artificial aging.

AIM: To assess the influence of finishing/polishing procedure on color stability (ΔE ) and surface roughness (R(a)) of composites (Heliomolar and Tetric - color A2) submitted to accelerated artificial aging (AAA). MATERIALS AND METHODS: Sixty test specimens were made of each composite (12 mm × 2 mm) and separated into six groups (n = 10), according to the type of finishing/polishing to which they were submitted: C, control; F, tip 3195 F; FF, tip 3195 FF; FP, tip 3195 F + diamond paste; FFP, tip 3195 FF + diamond paste; SF, Sof-Lex discs. After polishing, controlled by an electromechanical system, initial color (spectrophotometer PCB 6807 BYK GARDNER) and R(a) (roughness meter Surfcorder SE 1700, cut-off 0.25 mm) readings were taken. Next, the test specimens were submitted to the AAA procedure (C-UV Comexim) for 384 hours, and at the end of this period, new color readings and R(a) were taken. RESULTS: Statistical analysis [2-way analysis of variance (ANOVA), Bonferroni, P < 0.05] showed that all composites demonstrated ΔE alteration above the clinically acceptable limits, with the exception of Heliomolar composite in FP. The greatest ΔE alteration occurred for Tetric composite in SF (13.38 ± 2.10) statistically different from F and FF (P < 0.05). For R(a), Group F showed rougher samples than FF with statistically significant difference (P < 0.05). CONCLUSION: In spite of the surface differences, the different finishing/polishing procedures were not capable of providing color stability within the clinically acceptable limits.