Ageing of silorane-based and methacrylate-based composite resins: effects on translucency.

OBJECTIVES: Verify if media and time of storage affect the translucency of a silorane-based composite (Filtek P90) compared to two methacrylate-based composites (Z350 and ROK), and compare two methods of translucency evaluation. METHODS: Specimens were divided into two groups (n=7) according to the storage media (deionized water or red wine). With a spectrophotometer (SP60) in reflectance mode, the CIE L*a*b* parameters and opacity percentage readings were conducted at baseline, 24h, 30 days, and 180 days. Data were analyzed using two-way repeated measures ANOVA and Tukey (p<0.05). Pearson correlation measured the relationship between translucency parameter and opacity percentage. RESULTS: When stored in water, P90 showed an increase, whereas Z350 decreased in translucency. ROK did not exhibit any tendency over time. When stored in wine, the translucency of all materials decreased. A negative relationship was found between translucency parameter and opacity percentage. When stored in water, the a* values for P90 decreased, whereas Z350 and ROK showed values increasing over time. When stored in wine, the L* parameter tended to decrease over time, an effect that was less intense for P90. Moreover, the b* parameter for P90 decreased, whereas methacrylate-based composites increased over time. CONCLUSIONS: P90 was more stable in red wine than the other materials and became more translucent in water whether metacrilate-based materials became more opaque. Both media as well as storage time affected the translucency of the materials tested. Translucency could be measured with both methods tested. CLINICAL SIGNIFICANCE: Silorane-based composites seemed to be more stable than methacrylate-based composites in red wine and became more translucent over time in water, which was different than methacrylate-based composites. More studies are needed to clarify silorane-based composites performance.

Reflections about adhesive systems / Reflexiones acerca de los sistemas adhesivos

The adhesive systems are responsible for an efficient union between teeth and resin, resulting in a longevity restoration. They are organic molecules di or multifunctional that contain reactive groups that interact with dentin and with the resin monomer of composite resin. The adhesive systems are characterized by wet adhesion, which is a result of presence of hidrophylics radicals in their compositions, to promote a better bond and the best properties of the adhesion. Adhesive systems may use two different strategies to interact with the dental structure: total-etching and self-etching technique. The total-etching systems require a conditioning, a rinsing and a priming step in order to allow involvement of collagen fibers by the resin monomers and the formation of the so-called ‘hybrid layer’. The total-etching promotes the cleaning of dentin, also promotes superficial demineralization and delivers collagen fibrils to participate of an interface union mechanism teeth/ adhesive system/restorative material. Self-etching adhesive systems are characterized by demineralization and infiltration of resin monomers simultaneously. This technique is attractive because reduced sensitivity associated with retaining the smear layer and smear plugs, thereby, minimize the possibility of inadvertent contamination of the bonding surface with dentinal surface through dentinal fluid transudate.

Los sistemas adhesivos son responsables de una unión eficaz entre los dientes y la resina, dando como resultado una restauración durable. Son moléculas orgánicas bi o multifuncionales que contienen grupos reactivos que interactúan con la dentina y con el monómero de resina de composite. Los sistemas adhesivos se caracterizan por la adhesión húmeda, que es el resultado de la presencia de radicales hidrofílicos en sus composiciones, para promover una mejor adherencia y las mejores propiedades de la adhesión. Los sistemas adhesivos pueden utilizar dos estrategias diferentes para interactuar con la estructura dental: Técnica de grabado total y auto-grabado. Los sistemas de grabado total requiere un acondicionamiento, un lavado y un paso de priming con el fin de permitir la participación de las fibras de colágeno por los monómeros de resina y la formación de la llamada capa híbrida. El grabado total promueve la limpieza de la dentina, también promueve la desmineralización superficial y condiciona a las fibrillas de colágeno para participar de un mecanismo de interfaz de unión diente/sistema adhesivo /material de restauración. Los sistemas adhesivos autograbantes se caracterizan por la desmineralización y la infiltración de los monómeros de resina de forma simultánea. Esta técnica es atractiva debido a la sensibilidad reducida asociada a conservar la capa de barro dentinario y tapones de barro dentinario, reduciendo al mínimo la posibilidad de contaminación accidental de la superficie de unión con la superficie de la dentina a través del líquido dentinario trasudado.