Some road systems are unpaved due to limited governmental finance and fewer maintenance techniques. Such unpaved roads become vulnerable during heavy rainy seasons following restrained accessibility among cities and traffic accidents. Considering the circumstances, innovative and cost-effective approaches are required for unpaved roads. Microbially induced carbonate precipitation (MICP) is an emerging soil improvement technology using microbes to hydrolyze urea generating carbonate ions, and precipitates calcium carbonate in the presence of calcium ion. Induced calcium carbonate bonds soil particles enhancing stiffness and strength when the MICP reaction takes place within the soil system. This study introduces the use of microbes on unpaved road systems consisting of in situ lateritic soils. The MICP technology was implemented to improve soil strength through two approaches: surface spraying and mixing methods. A series of soil testing was performed with varying chemical concentrations to measure precipitation efficiency, strength, and quality for construction material and see the feasibility of the proposed methods. The laboratory test results indicated that the surface spraying method provided improved; however, it was highly affected by the infiltration characteristics of used soils. The mixing method showed promising results even under submerged conditions, but still required improvement. Overall, the proposed idea seems possible to apply to improving unpaved road systems in the lateritic region but requires further research and optimization.
RESUMO
Ground-granulated blast-furnace slag (GGBFS) can be used as a cementless binder after activation. Recent approaches to activate GGBFS have focused on chemical methods that use NaOH, KOH, and CaO. This study introduces the use of bacteria to activate GGBFS as a biological approach. The presence of bacteria (volumetric ratio), curing temperature (23 °C and 60 °C), and number of curing days (3, 7, and 28 d) are investigated. The use of urea is considered owing to the possibility of calcium carbonate formation. The activated GGBFS is evaluated in the form of a cube (5 cm × 5 cm × 5 cm) for its strength, mineral identification, and pore size distribution. A brick (19 cm × 9 cm × 5.7 cm) is prefabricated to see the feasibility of commercializing bacteria-activated GGBFS based on water absorption and strength measurements. All results are compared with those of water-activated GGBFS. The results indicate that the use of urea inhibits the strength improvement of bacteria-activated GGBFS. Bacterial suspension enhances the GGBFS strength at a curing temperature of 60 °C. Mineral identification tests show that the strength increase is primarily due to the formation of calcite. The compressive strength satisfies the commercial standard of concrete bricks; however, the water absorption rate must be resolved.