Tissue-susceptibility matched carbon nanotube electrodes for magnetic resonance imaging.

Test disk electrodes were fabricated from carbon nanotubes (CNT) using the Carbon Nanotube Templated Microfabrication (CNT-M) technique. The CNT-M process uses patterned growth of carbon nanotube forests from surfaces to form complex patterns, enabling electrode sizing and shaping. The additional carbon infiltration process stabilizes these structures for further processing and handling. At a macroscopic scale, the electrochemical, electrical and magnetic properties, and magnetic resonance imaging (MRI) characteristics of the disk electrodes were investigated; their microstructure was also assessed. CNT disk electrodes showed electrical resistivity around 1â€¯Ω·cm, charge storage capacity between 3.4 and 38.4 mC/cm2, low electrochemical impedance and magnetic susceptibility of -5.9 to -8.1 ppm, closely matched to that of tissue (∼-9 ppm). Phantom MR imaging experiments showed almost no distortion caused by these electrodes compared with Cu and Pt-Ir reference electrodes, indicating the potential for significant improvement in accurate tip visualization.

Fabrication of High Aspect Ratio Millimeter-Tall Free-Standing Carbon Nanotube-Based Microelectrode Arrays.

Microelectrode arrays of carbon nanotube (CNT)/carbon composite posts with high aspect ratio and millimeter-length were fabricated using carbon-nanotube-templated microfabrication with a sacrificial "hedge". The high aspect ratio, mechanical robustness, and electrical conductivity of these electrodes make them a potential candidate for next-generation neural interfacing. Electrochemical measurements were also demonstrated using an individual CNT post microelectrode with a diameter of 25 µm and a length of 1 mm to perform cyclic voltammetry on both methyl viologen and dopamine in a phosphate-buffered saline solution. In addition to detection of the characteristic peaks, the CNT post microelectrodes show a fast electrochemical response, which may be enabling for in vivo and/or in vitro measurements. The CNT post electrode fabrication process was also integrated with other microfabrication techniques, resulting in individually addressable electrodes.