Highly Selective CO2 Hydrogenation to Methanol over Complex In/Co Catalysts: Effect of Polymer Frame.

The growing demand for new energy sources governs the intensive research into CO2 hydrogenation to methanol, a valuable liquid fuel. Recently, indium-based catalysts have shown promise in this reaction, but they are plagued by shortcomings such as structural instability during the reaction and low selectivity. Here, we report a new strategy of controlling the selectivity and stability of bimetallic magnetically recoverable indium-based catalysts deposited onto a solid support. This was accomplished by the introduction of a structural promoter: a branched pyridylphenylene polymer (PPP). The selectivity of methanol formation for this catalyst reached 98.5%, while in the absence of PPP, the catalysts produced a large amount of methane, and the selectivity was about 70.2%. The methanol production rate was higher by a factor of twelve compared to that of a commercial Cu-based catalyst. Along with tuning selectivity, PPP allowed the catalyst to maintain a high stability, enhancing the CO2 sorption capacity and the protection of In against sintering and over-reduction. A careful evaluation of the structure-activity relationships allowed us to balance the catalyst composition with a high level of structural control, providing synergy between the support, magnetic constituent, catalytic species, and the stabilizing polymer layer. We also uncovered the role of each component in the ultimate methanol activity and selectivity.

Metal-Ion Distribution and Oxygen Vacancies That Determine the Activity of Magnetically Recoverable Catalysts in Methanol Synthesis.

Here, we report on the development of novel Zn-, Zn-Cr-, and Zn-Cu-containing catalysts using magnetic silica (Fe3O4-SiO2) as the support. Transmission electron microscopy, powder X-ray diffraction, and X-ray photoelectron spectroscopy (XPS) showed that the iron oxide nanoparticles are located in mesoporous silica pores and the magnetite (spinel) structure remains virtually unchanged despite the incorporation of Zn and Cr. According to XPS data, the Zn and Cr species are intermixed within the magnetite structure. In the case of the Zn-Cu-containing catalysts, a separate Cu2O phase was also observed along with the spinel structure. The catalytic activity of these catalysts was tested in methanol synthesis from syngas (CO + H2). The catalytic experiments showed an improved catalytic performance of Zn- and Zn-Cr-containing magnetic silicas compared to that of the ZnO-SiO2 catalyst. The best catalytic activity was obtained for the Zn-Cr-containing magnetic catalyst prepared with 1 wt % Zn and Cr each. X-ray absorption spectroscopy demonstrated the presence of oxygen vacancies near Fe and Zn in Zn-containing, and even more in Zn-Cr-containing, magnetic silica (including oxygen vacancies near Cr ions), revealing a correlation between the catalytic properties and oxygen vacancies. The easy magnetic recovery, robust synthetic procedure, and high catalytic activity make these catalysts promising for practical applications.