RESUMO
Graded porous inorganic materials directed by macromolecular self-assembly are expected to offer unique structural platforms relative to conventional porous inorganic materials. Their preparation to date remains a challenge, however, based on the sparsity of viable synthetic self-assembly pathways to control structural asymmetry. Here we demonstrate the fabrication of graded porous carbon, metal, and metal oxide film structures from self-assembled block copolymer templates by using various backfilling techniques in combination with thermal treatments for template removal and chemical transformations. The asymmetric inorganic structures display mesopores in the film top layers and a gradual pore size increase along the film normal in the macroporous sponge-like support structure. Substructure walls between macropores are themselves mesoporous, constituting a structural hierarchy in addition to the pore gradation. Final graded structures can be tailored by tuning casting conditions of self-assembled templates as well as the backfilling processes. We expect that these graded porous inorganic materials may find use in applications including separation, catalysis, biomedical implants, and energy conversion and storage.
RESUMO
A facile method for forming asymmetric organic-inorganic hybrid membranes for selective separation applications is developed. This approach combines co-assembly of block copolymer (BCP) and inorganic nanoparticles (NPs) with non-solvent induced phase separation. The method is successfully applied to two distinct molar mass BCPs with different fractions of titanium dioxide (TiO2) NPs. The resulting hybrid membranes exhibit structural asymmetry with a thin nanoporous surface layer on top of a macroporous fingerlike support layer. Key parameters that dictate membrane surface morphology include the fraction of inorganics used and the length of time allowed for surface layer development. The resulting membranes exhibit both good selectivity and high permeability (3200 ± 500 Lm(-2) h(-1) bar(-1)). This fast and straightforward synthesis method for asymmetric hybrid membranes provides a new self-assembly platform upon which multifunctional and high-performance organic-inorganic hybrid membranes can be formed.
Assuntos
Membranas/química , Nanopartículas/química , Titânio/química , Compostos Orgânicos/química , Polímeros/químicaRESUMO
Novel platinum nanowheels were synthesized by the reduction of aqueous platinum complex with ascorbic acid in the presence of disk-like bicelles. The platinum nanowheels possess thickened centers and flared edges that are connected by dendritic platinum nanosheets. This structural complexity can be attributed to the inhomogeneous micro-environment of the templating bicelles consisting of a central bi-layer region and a high curvature rim. The formation mechanism of the nanowheels was investigated by imaging nanostructures at different stages of the reaction. The templating bicelles were also imaged by TEM with the aid of negative staining. The variation of reaction parameters including platinum concentration, temperature, and total concentration of surfactants (CTAB + FC7) led to other types of platinum nanostructures, such as circular dendritic nanosheets with a tunable diameter and rectangular dendritic nanosheets. Interestingly, under irradiation by a TEM electron beam, the dendritic nanosheet portion of the nanowheels transforms into a metastable holey sheet. In addition, the platinum nanowheels have an electrochemical active surface area comparable to that of ETEK platinum black and thus are expected to have potential applications in catalysis.
RESUMO
Under electron-beam irradiation, dendritic platinum nanosheets structurally evolve into metastable "holey" nanosheets. Monte Carlo simulations of this structural transformation agree well with electron microscope images detailing the ripening process. The experiments and simulations show that nanoscale holes of a critical size are persistent and give holey sheets their morphological stability and sustained high surface area. Platinum nanostructures composed of these holey nanosheets exhibit improved durability in electrocatalytic reactions due to their remarkable ripening resistance.
RESUMO
Disk-like surfactant bicelles provide a unique meso-structured reaction environment for templating the wet-chemical reduction of platinum(II) salt by ascorbic acid to produce platinum nanowheels. The Pt wheels are 496 +/-55 nm in diameter and possess thickened centers and radial dendritic nanosheets (about 2-nm in thickness) culminating in flared dendritic rims. The structural features of the platinum wheels arise from confined growth of platinum within the bilayer that is also limited at edges of the bicelles. The size of CTAB/FC7 bicelles is observed to evolve with the addition of Pt(II) complex and ascorbic acid. Synthetic control is demonstrated by varying the reaction parameters including metal salt concentration, temperature, and total surfactant concentration. This study opens up opportunities for the use of other inhomogeneous soft templates for synthesizing metals, metal alloys, and possibly semiconductors with complex nanostructures.
Assuntos
Nanopartículas Metálicas/química , Platina/química , Ácido Ascórbico/química , Dendrímeros/síntese química , Dendrímeros/química , Micelas , Microscopia Eletrônica de Transmissão , Tensoativos/químicaRESUMO
Hollow platinum nanospheres that are porous and have uniform shell thickness are prepared by templating platinum growth on polystyrene beads with an adsorbed porphyrin photocatalyst irradiated by visible light.
RESUMO
Platinum nanowire networks have been synthesized by chemical reduction of a platinum complex using sodium borohydride in the presence of a soft template formed by cetyltrimethylammonium bromide in a two-phase water-chloroform system. The interconnected polycrystalline nanowires possess the highest surface area (53 +/- 1 m2/g) and electroactive surface area (32.4 +/- 3.6 m2/g) reported for unsupported platinum nanomaterials; the high surface area results from the small average diameter of the nanowires (2.2 nm) and the 2-10 nm pores determined by nitrogen adsorption measurements. Synthetic control over the network was achieved simply by varying the stirring rate and reagent concentrations, in some cases leading to other types of nanostructures including wormlike platinum nanoparticles. Similarly, substitution of a palladium complex for platinum gives palladium nanowire networks. A mechanism of formation of the metal nanowire networks is proposed based on confined metal growth within a soft template consisting of a network of swollen inverse wormlike micelles.