RESUMO
AIM: To evaluate the bleaching efficacy and effects on enamel properties of experimental gels with carbamide peroxide (CP; 10%) or hydrogen peroxide (HP; 6%) containing calcium polyphosphate sub-microparticles (CaPPs). METHODS: A total of 216 bovine tooth specimens were divided for microhardness and color analyses (n = 108) and block randomized into nine groups (n = 12): (G1) commercial CP (Whiteness Perfect, FGM; Brazil); (G2) experimental CP; (G3) CP-0.5%CaPPs; (G4) CP-1.5%CaPPs; (G5) commercial HP (Potenza Bianco, PHS; Brazil); (G6) experimental HP; (G7) HP-0.5%CaPPs; (G8) HP-1.5%CaPPs; (G9) artificial saliva. The gels' pH values were determined with a bench pH meter. Color (ΔE, ΔE00, ΔWID) and microhardness variation were evaluated before and after the therapy. Part of the specimens used for microhardness was submitted to the scanning electron microscopy (SEM) (n = 3) and energy-dispersive X-ray spectroscopy EDX (n = 3) analyses. Statistical analyses were performed in the R statistical software (α = 0.05). Linear mixed models for repeated measures in time were used to analyze microhardness and L* values. Generalized linear models were used to analyze the a*, b*, ΔE, ΔE00, and ΔWID, considering a group effect. The EDX data were analyzed using a one-way ANOVA with Tukey's test. RESULTS: The gels' pH remained over 6,0. All gels effectively bleached the specimens and did not differ significantly. When compared to the control group, the hardness was significantly lower in the G1, G2, G6, and G7 groups. The G3, G4, G5, and G8 groups did not differ significantly (p > 0.05). CONCLUSION: The incorporation of CaPPs in low-concentration whitening gels reduces its negative effects on microhardness without interfering with their bleaching efficacy.
RESUMO
OBJECTIVE: To assessed the physical and chemical properties of human-enamel after treatment with an experimental bleaching gel containing 35%-hydrogen peroxide (HP) and calcium polyphosphate sub-microparticles (CaPP). MATERIALS AND METHODS: Enamel/dentin specimens (4 × 4 × 3 mm) were obtained (n = 120) and allocated to different groups: control (saliva only); experimental (HP35%); commercial (whiteness-HP-Maxx); CaPP0.5% (HP35% + CaPP0.5wt%); CaPP1.5% (HP35% + CaPP1.5wt%). Three sessions were performed. The specimens' color was assessed using a spectrophotometer and the color (ΔE/ΔE00) and bleaching index (ΔWID) determined. The surface roughness and microhardness were assessed with a roughness tester and Knoop indenter. Raman spectroscopy was performed to obtain the ratios between the areas under the 431, 580, and 1070 cm-1 and the 960 cm-1 bands (430:960, 580:960, 1070:960). Kruskal-Wallis and Dunn compared the color, Ra, and SMH data. The Raman data was analyzed with Kruskal-Wallis and Dunn (α = 5%). RESULTS: The ΔE, ΔE00, and ΔWID were similar among the bleached groups (p > 0.05). The roughness was not different between the groups (p > 0.05). After the 3rd session, CaPP0.5% had higher microhardness than the experimental (p < 0.05). The 1070:960 was higher in the experimental than in the CaPP1.5% and control (p < 0.05). CONCLUSIONS: In human enamel, CaPP did not alter the bleaching effectiveness or roughness, and additionally, CaPP-containing gels increased the microhardness and preserved the mineral content when compared to the experimental without CaPP. CLINICAL RELEVANCE: Experimental bleaching gels containing calcium polyphosphate sub-microparticles as a mineral source reduce the mineral content alteration and superficial microhardness reduction, known potential side effects of the in-office bleaching treatments.