Preparation, characterization and properties of nano-hydroxyapatite/polypropylene carbonate biocomposite.

The combination of nano-hydroxyapatite (n-HA) and polypropylene carbonate (PPC) was used to make a composite materials by a coprecipitation method. The physical and chemical properties of the composite were tested. Scanning electron microscope (SEM) observation indicated that the biomimetic n-HA crystals were uniformly distributed in the polymer matrix. As the n-HA content increased in the composite, the fracture mechanism of the composites changes from gliding fracture to gliding and brittle fracture. Furthermore, the chemical interaction between inorganic n-HA and polypropylene carbonate was also investigated and discussed in detail. The hydrogen bonds might be formed between -OH/CO3(2-) of n-HA crystal and the ester group (-COO-) of PPC. The tensile strength of n-HA/PPC (40/60) was similar to that of the cancellous bone, and reached ca 58 MPa. The osteoblasts were cultured for up to 7 days, and then the adhesion and proliferation of osteoblasts were measured by Methyl thiazolyl tetrazolium (MTT) colorimetry assay and SEM. The cells proliferated, grew normally in fusiform shape and well attached. The in vitro test confirmed that the n-HA/PPC composites were biocompatible and showed undetectable negative effect on osteoblasts. In vivo implantation of the composite in New Zealand white rabbits was performed. It can stimulate the growth of a new bone, and at the same time the material begins to degrade. These results suggested that the composite may be suitable for the reparation or replacement of bone defects and possessed the potential for clinical applications.

[Synthesis and characterization of CO-3(2-) doping nano-hydroxyapatite].

CO3(2-) doping is an effective method to increase the biological activity of nano-hydroxyapatite (n-HA). In the present study, calcium nitrate and trisodium phosphate were chosen as raw materials, with a certain amount of Na2CO3 as a source of CO-3(2-) ions, to synthesize nano-carbonate hydroxyapatite (n-CHA) slurry by solution precipitation method. The structure and micro-morphology of n-CHA were characterized by transmission electron microscope (TEM), X-ray diffraction (XRD), Fourier transform-infrared spectroscopy (FTIR) and Raman spectroscopy (RS). The results revealed that the synthetic n-HA crystals are acicular in nanometer scale and have a crystal size of 20-30 nm in diameter and 60-80 nm in length, which are similar to natural bone apatite. And the crystallinity of n-CHA crystals decreases to the increment of CO3(2-). Samples with more CO3(2) have composition and structure more similar to the bone apatite. The value of lattice parameters a decreases, value of c increases, and c/a value increases with the increase in the amount of CO3(2-), in accordance with crystal cell parameters change rule of type B replacement. In the AB mixed type (substitution OH- and PO4(3-)) CHA, IR characteristic peak of CO3(2-) out-of-plane bending vibration appears at 872 cm(-1), meanwhile, the asymmetry flexible vibration band is split into band at 1 454 cm(-1) and band at 1 420 cm(-1), while weak CO3(2)-peak appears at 1 540 cm(-1). CO3(2-) Raman peak of symmetric stretching vibration appears at 1 122 cm(-1). CO3(2-) B-type (substitution PO4(3-)) peak appeared at 1 071 cm(-1). Through the calculation of integral area ratio of PO4(3-)/ CO3(2-), OH-/CO3(2-), and PO4(3-)/OH-, low quantity CO3(2-) is B-type and high quantity CO3(2-) is A-type (substitution OH-). The results show that the synthesized apatite crystals are AB hybrid substitued nano-carbonate hydroxyapatite, however B-type replacement is the main substitute mode. Due to similarity inthe shape, size, crystal structure and growth mode, the synthesized apatite crystals can be called a kind of bone-like apatite.