Effect of Cold Drawing and Annealing in Thermomechanical Treatment Route on the Microstructure and Functional Properties of Superelastic Ti-Zr-Nb Alloy.

In this study, a superelastic Ti-18Zr-15Nb (at. %) alloy was subjected to thermomechanical treatment, including cold rotary forging, intermediate annealing, cold drawing, post-deformation annealing, and additional low-temperature aging. As a result of intermediate annealing, two structures of ß-phase were obtained: a fine-grained structure (d ≈ 3 µm) and a coarse-grained structure (d ≈ 11 µm). Cold drawing promotes grain elongation in the drawing direction; in a fine-grained state, grains form with a size of 4 × 2 µm, and in a coarse-grained state, they grow with a size of 16 × 6 µm. Post-deformation annealing (PDA) at 550 °C for 30 min leads to grain sizes of 5 µm and 3 µm, respectively. After PDA at 550 °C (30 min) in the fine-grained state, the wire exhibits high tensile strength (UTS = 624 MPa), highest elongation to failure (δ ≥ 8%), and maximum difference between the dislocation and transformation yield stresses, as well as the highest superelastic recovery strain (εrSE ≥ 3.3%) and total elastic + superelastic recovery strain (εrel+SE ≥ 5.4%). Additional low-temperature aging at 300 °C for 30-180 min leads to ω-phase formation, alloy hardening, embrittlement, and a significant decrease in superelastic recovery strain.

Effect of Thermomechanical Treatment on Structure and Functional Fatigue Characteristics of Biodegradable Fe-30Mn-5Si (wt %) Shape Memory Alloy.

The Fe-Mn-Si shape memory alloys are considered promising materials for the biodegradable bone implant application since their functional properties can be optimized to combine bioresorbability with biomechanical and biochemical compatibility with bone tissue. The present study focuses on the fatigue and corrosion fatigue behavior of the thermomechanically treated Fe-30Mn-5Si (wt %) alloy compared to the conventionally quenched alloy because this important functionality aspect has not been previously studied. Hot-rolled and water-cooled, cold-rolled and annealed, and conventionally quenched alloy samples were characterized by X-ray diffraction, transmission electron microscopy, tensile fatigue testing in air atmosphere, and bending corrosion fatigue testing in Hanks' solution. It is shown that hot rolling at 800 °C results in the longest fatigue life of the alloy both in air and in Hanks' solution. This advantage results from the formation of a dynamically recrystallized γ-phase grain structure with a well-developed dislocation substructure. Another important finding is the experimental verification of Young's modulus anomalous temperature dependence for the studied alloy system, its minimum at a human body temperature, and corresponding improvement of the biomechanical compatibility. The idea was realized by lowering Ms temperature down to the body temperature after hot rolling at 800 °C.

The Electrochemical and Mechanical Behavior of Bulk and Porous Superelastic Ti‒Zr-Based Alloys for Biomedical Applications.

Titanium alloys are well recognized as appropriate materials for biomedical implants. These devices are designed to operate in quite aggressive human body media, so it is important to study the corrosion and electrochemical behavior of the novel materials alongside the underlying chemical and structural features. In the present study, the prospective Ti‒Zr-based superelastic alloys (Ti-18Zr-14Nb, Ti-18Zr-15Nb, Ti-18Zr-13Nb-1Ta, atom %) were analyzed in terms of their phase composition, functional mechanical properties, the composition and structure of surface oxide films, and the corresponding corrosion and electrochemical behavior in Hanks' simulated biological solution. The electrochemical parameters of the Ti-18Zr-14Nb material in bulk and foam states were also compared. The results show a significant difference in the functional performance of the studied materials, with different composition and structure states. In particular, the positive effect of the thermomechanical treatment regime, leading to the formation of a favorable microstructure on the corrosion resistance, has been revealed. In general, the Ti-18Zr-15Nb alloy exhibits the optimum combination of functional characteristics in Hanks' solution, while the Ti-18Zr-13Nb-1Ta alloy shows the highest resistance to the corrosion environment. The Ti-18Zr-14Nb-based foam material exhibits slightly lower passivation kinetics as compared to its bulk equivalent.