RESUMO
The crystalline selenido germanates [Li4(H2O)16][Ge4Se10]·4.3H2O (1), [{Li4(thf)12}Ge4Se10] (2), and [Li2(H2O)8][MnGe4Se10] (3) (thf = THF = tetrahydrofuran) were obtained by an extraction of a glassy ternary phase of the nominal composition Li4Ge4Se10 (=Li2S·2GeSe2) with water (1) or THF (2) and slow evaporation of the solvent or by being layered with MnBr2 in H2O/MeOH (3), respectively. The compounds contain known selenido germanate anions, however, for the first time with Li+ counterions. This is especially remarkable for the prominent ∞3{[MnGe4Se10]2-} open-framework structure, which was reported to crystallize with (NMe4)+, Cs+, Rb+, and K+ counterions, but it has not yet been realized with the smallest alkali metal cation. Impedance spectroscopic studies on Li4Ge4Se10 classify the glassy solid as a moderate Li+ ion conductor.
RESUMO
Highly conductive solid electrolytes are crucial to the development of efficient all-solid-state batteries. Meanwhile, the ion conductivities of lithium solid electrolytes match those of liquid electrolytes used in commercial Li+ ion batteries. However, concerns about the future availability and the price of lithium made Na+ ion conductors come into the spotlight in recent years. Here we present the superionic conductor Na11 Sn2 PS12 , which possesses a room temperature Na+ conductivity close to 4â mS cm-1 , thus the highest value known to date for sulfide-based solids. Structure determination based on synchrotron X-ray powder diffraction data proves the existence of Na+ vacancies. As confirmed by bond valence site energy calculations, the vacancies interconnect ion migration pathways in a 3D manner, hence enabling high Na+ conductivity. The results indicate that sodium electrolytes are about to equal the performance of their lithium counterparts.