Antibiofilm Activity of Polyamide 11 Modified with Thermally Stable Polymeric Biocide Polyhexamethylene Guanidine 2-Naphtalenesulfonate.

The choice of efficient antimicrobial additives for polyamide resins is very difficult because of their high processing temperatures of up to 300 °C. In this study, a new, thermally stable polymeric biocide, polyhexamethylene guanidine 2-naphtalenesulfonate (PHMG-NS), was synthesised. According to thermogravimetric analysis, PHMG-NS has a thermal degradation point of 357 °C, confirming its potential use in joint melt processing with polyamide resins. Polyamide 11 (PA-11) films containing 5, 7 and 10 wt% of PHMG-NS were prepared by compression molding and subsequently characterised by FTIR spectroscopy. The surface properties were evaluated both by contact angle, and contactless induction. The incorporation of 10 wt% of PHMG-NS into PA-11 films was found to increase the positive surface charge density by almost two orders of magnitude. PA-11/PHMG-NS composites were found to have a thermal decomposition point at about 400 °C. Mechanical testing showed no change of the tensile strength of polyamide films containing PHMG-NS up to 7 wt%. Antibiofilm activity against the opportunistic bacteria Staphylococcus aureus and Escherichia coli was demonstrated for films containing 7 or 10 wt% of PHMG-NS, through a local biocide effect possibly based on an influence on the bacterial eDNA. The biocide hardly leached from the PA-11 matrix into water, at a rate of less than 1% from its total content for 21 days.

New promising antifouling agent based on polymeric biocide polyhexamethylene guanidine molybdate.

A new polymeric biocide polyhexamethylene guanidine (PHMG) molybdate has been synthesized. The obtained cationic polymer has limited water solubility of 0.015 g/100 mL and is insoluble in paint solvents. The results of acute toxicity studies indicate moderate toxicity of PHMG molybdate, which has a median lethal dose at 48 h of 0.7 mg/L for Daphnia magna and at 96 h of 17 mg/L for Danio rerio (zebrafish) freshwater model organisms. Commercial ship paint was then modified by the addition of a low concentration of polymeric biocide 5% (w/w). The painted steel panels were kept in Dnipro River water for the evaluation of the dynamics of fouling biomass. After 129-d exposure, Bryozoa dominated in biofouling of tested substrates, forming 86% (649 g/m2 ) of the total biomass on control panel surfaces. However, considerably lower Bryozoa fouling biomass (15 g/m2 ) was detected for coatings containing PHMG molybdate. Dreissenidae mollusks were found to form 88% (2182 g/m2 ) of the fouling biomass on the control substrates after 228 d of exposure, whereas coatings containing PHMG molybdate showed a much lower biomass value of 23.6 g/m2 . The leaching rate of PHMG molybdate in water was found to be similar to rates for conventional booster biocides ranging from 5.7 µg/cm2 /d at the initial stage to 2.2 µg/cm2 /d at steady state. Environ Toxicol Chem 2017;36:2543-2551. © 2017 SETAC.