BMC Chem ; 18(1): 21, 2024 Jan 28.
Artigo em Inglês | MEDLINE | ID: mdl-38281010

RESUMO

Aluminum corrosion inhibitors "{[CuI (CN)2(phen) CuII (CN)2(phen)]5H2O},(MOF1) and {[CuI(CN)2(phen)CuII(CN)2(phen)]5H2O}@TiO2 (MOF1@TiO2) were studied in one molar HCl solution". The ML results for three different temperatures (25-45 °C) were compared with the results of PDP and EIS analyses. The adsorption of inhibitors on Al surfaces has been calculated and discussed by a Langmuir isotherm. The inhibitors that were created showed great effectiveness, with a noticeable increase in their inhibitory efficiency as the dosage was raised and the temperature was lowered. Inhibition efficiency each amounted to 88.6%, 84.5% at 400 ppm and 25 °C for MOF1@TiO2 and MOF1, respectively. Analyzing the polarization curves of synthesized inhibitors revealed that they were mixed-type inhibitors. Al was found to be surface inhibited when coated with a thin film of inhibitors, and "Al's surface morphology was assessed by different techniques such as scanning electron microscopy (SEM), energy dispersive X-ray (EDX) and atomic force microscope (AFM)". "Theoretical models like quantum chemical and molecular dynamics simulation authenticated the experimental observation". The MOFs exhibit exceptional corrosion resistance against Al when exposed to acidic environments, according to several tests.

2.
RSC Adv ; 11(41): 25314-25333, 2021 Jul 19.
Artigo em Inglês | MEDLINE | ID: mdl-35478921

RESUMO

This study targets the investigation of three pyrimidine-bichalcophene derivatives (MA-1230, MA-1231, MA-1232) for the prevention of corrosion on copper in 1 M HNO3 via weight loss (WL), potentiodynamic polarization (PDP), and electrochemical impedance spectroscopy (EIS) techniques. The surface morphology was also analyzed by different methods. It was found that the inhibition efficiency (% η) increased by increasing the doses of pyrimidine derivatives and the temperature of the medium. Weight loss data revealed the better adsorption of MA-1232 on the Cu surface at increased inhibitor dose, reaching a maximum efficiency of 99.14% at a dose of 21 µM at 45 °C. The best description of the adsorption of the investigated derivatives on the copper surface was given by the Langmuir isotherm. Some important thermodynamic parameters for the studied inhibitors were computed and are discussed herein. The polarization studies showed that the pyrimidine-bichalcophenes act as mixed inhibitors. Computational chemical approaches were used with informative yields, including quantum-chemical and molecular dynamics simulation techniques, which agree with the experimental results. The results obtained from all tested methods are strongly accepted.