Green synthesis and characterization of binary, ternary, and quaternary Ti/MMO anodes for chlorine and oxygen evolution reactions.

Dimensionally stable anodes of titanium (Ti) metal coated with mixed metal oxides (MMO) are widely used in several electrochemical applications, especially chloro-alkali electrolysis. Herein, we deposited MMO coatings on Ti substrates in different compositions, namely, (60%RuO2-40%TiO2), (60%RuO2-30%TiO2-10%IrO2), and (60%RuO2-20%TiO2-15%IrO2-5%Ta2O5), where RuO2 has the same percentage ratio in all coatings. The aim was to use these electrodes for chlorine evolution reaction (CER) and oxygen evolution reaction (OER) applications. Electrochemical characterization of the coated samples was performed to identify the best Ti/MMO electrodes with the highest efficiencies among the various prepared combinations. The role of IrO2 and Ta2O5 in enhancing corrosion resistance and electrochemical efficacy was up for debate. Scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) analyses were exploited to determine the surface morphology, chemical composition, crystallinity, surface composition, and chemical states of the acquired coatings. The differential scanning calorimetry (DSC) method was used to evaluate the apparent activation energy ( E a ) of the deposited MMO. Additionally, the electrochemical performance of our designed coatings was scrutinized by cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), a current on-off test, a CV stability test (ST), and an accelerated stability test (AST). Furthermore, linear sweep voltammetry (LSV) was incorporated to assess the catalytic efficacy of the prepared anodes toward the CER in a brine solution of pH 2 and the OER in 1 M H2SO4. It became clear that the CER and OER incurred almost the same potential value (1.1 V) on both Ti/RuO2-TiO2 and Ti/RuO2-TiO2-IrO2 electrodes. However, on the Ti/RuO2-TiO2-IrO2-Ta2O5 anode, there was a 0.2 V potential difference between the CER occurring at 1.1 V and the OER happening at 1.3 V.

Molecularly imprinted polymer-based bulk optode for the determination of itopride hydrochloride in physiological fluids.

We report here for the first time on the use of Molecularly Imprinted Polymers as modifiers in bulk optodes, Miptode, for the determination of a pharmaceutical compound, itopride hydrochloride as an example in a concentration range of 1×10(-1)-1×10(-4)molL(-1). In comparison to the optode containing the ion exchanger only (Miptode 3), the optode containing the ion exchanger and the MIP particles (Miptode 2) showed improved selectivity over the most lipophilic species, Na(+) and K(+), by more than two orders of magnitude. For instance, the optical selectivity coefficients using Miptode 2, [Formula: see text] , were as follow: NH4(+)˂-6; Na(+)=-4.0, which were greatly enhanced in comparison with that obtained by Miptode 3. This work opens a new avenue for using miptodes for the determination of all the pharmaceutical preparations without the need for the development of new ionophores.

Conductimetric determination of reproterol HCl and pipazethate HCl and salbutamol sulphate in their pharmaceutical formulations.

A simple and sensitive conductimetric method for the determination of salbutamol sulphate and reproterol and pipazethate hydrochlorides is presented based on their ion associates with phosphotungstic and phosphomolybdic acids. The effect of solvent, molar ratio, reagent concentration and temperature were studied, and the solubility products of the formed ion associates were calculated. The method was applied to the determination of the drugs in their pure state or pharmaceutical preparations with mean recovery values of 99.82-100.54, 99.75-100.12 and 99.95-100.40%, and coefficient of variation 0.28-0.52, 0.16-0.36 and 0.19-0.33 for salbutamol sulphate, reproterol HCl and pipazathate HCl, respectively.

Flow injection potentiometric determination of pipazethate hydrochloride.

New plastic membrane electrodes for pipazethate hydrochloride based on pipazethatium phosphotungstate, pipazethatium phosphomolybdate and a mixture of the two were prepared. The electrodes were fully characterized in terms of composition, life span, pH and temperature and were then applied to the potentiometric determination of the pipazethate ion in its pure state and pharmaceutical preparations under batch and flow injection conditions. The selectivity of the electrodes towards many inorganic cations, sugars and amino acids was also tested.