Evolution of the polymorph selectivity of titanium dioxide was studied under acidic and low-temperature synthesis conditions. Short synthesis times resulted in high relative amounts of the rutile phase, and long synthesis times resulted in high relative amounts of the brookite and anatase phases. The effect of titania precursor concentration was investigated and found to have a large impact on the polymorph selectivity. As the reaction proceeds with time, changes in the chemical environment, caused in particular by the gradually decreasing titania precursor concentration, are therefore likely the cause of the change in polymorph selectivity observed.
RESUMO
Core-shell microcapsules consisting of a titanium dioxide shell and a hydrophobic solvent core have been prepared with diameters of a few micrometers and a narrow size distribution using a simple and fast airbrush technique. These microcapsules were prepared at room temperature in a single-step process in which an oil with a dissolved titanium alkoxide precursor was forced together with an aqueous solution, containing a surface-active polymer, through a narrow spray nozzle using a nitrogen gas propellant. Several different parameters of chemical, physical, and processing origin were investigated to find an optimal recipe. Two different alkanes, one ketone, and four alcohols were tested and evaluated as core materials, alone or together with the antifungal biocide 2-n-octyl-4-isothiazolin-3-one (OIT). Long-chain alcohols were found suitable as core oil due to their low solubility in water and surface activity. The addition of the surface-active polymers in the water phase was important in aiding the formation and stabilization of the titanium dioxide shell. An impressive loading of 50 wt% of the semi-hydrophobic OIT was possible to encapsulate using this simple and applicable procedure.