RESUMO
Abstract Cetrimide (CTR) is a cationic surfactant detergent with antimicrobial and antibiofilm activity. The aim of this study was to evaluate setting time, pH, solubility and antibiofilm activity of tricalcium silicate cement (TSC) with zirconium oxide (ZrO2) and its association with 0.2 and 0.4% cetrimide. Initial and final setting times (IST and FST) were assessed based on ISO-6876. pH was evaluated at periods of 1,3,7,14 and 21 days. Solubility was analyzed by weight loss. A modified direct contact test (MDCT) on the biofilm of Enterococcus faecalis formed on bovine root dentin blocks was performed, after 6 hours of manipulation and 15 hours of contact time. The analysis was performed by UFC mL ¯¹ counting. The data were analyzed by ANOVA and Tukey's tests (α=0.05). Higher IST was observed for TSC/ZrO2+CTR in both concentrations than for TSC/ZrO2 and lower FST for TSC/ZrO2+0.4% CTR (p0.05). All materials exhibited increased mass. TSC/ZrO2+CTR 0.4% had lower mass gain than the other materials (p<0.05). The highest antibiofilm activity was observed for TSC/ZrO2+CTR in both concentrations, when compared with the positive control (p<0.05). In conclusion, CTR exhibited potential to promote greater antibiofilm activity to tricalcium silicate cement, without harming its physicochemical properties of setting time, pH and solubility.
Resumen Cetrimida (CTR) es un detergente y surfactante catiónico con actividad antimicrobiana y antibiofilm. El objetivo de este estudio fue evaluar el tiempo de fraguado, pH, solubilidad y actividad antibiofilm del cemento de silicato tricálcico (CST) con óxido de zirconio (ZrO2) y su asociación con CTR a 0.2% y 0.4%. Tiempo de fraguado inicial y final (TFI y TFF) fueron determinados con base en las normas ISO-6876. pH fue evaluado en los períodos de 1,3, 7,14 y 21 días. Solubilidad fue analizada por la pérdida de masa/peso. El test de contacto directo modificado (TCDM) fue realizado sobre biofilm de Enterococcus faecalis formado en dentina radicular bovina, después de 6 horas de manipulación de los cementos y 15 horas de contacto. El análisis fue realizado por la cuantificación de UFC mL¯¹. Los datos fueron analizados usando las pruebas de ANOVA y Tukey (α=0.05). Mayor TFI fue observado para CST/ ZrO2+CTR en las dos concentraciones que para TSC/ZrO2 y menor TFF para TSC/ ZrO2+CTR 0.4% (p0.05). Todos los materiales mostraron aumento de masa. TSC/ZrO2+CTR 0.4% tuvo menor gano de masa que los otros materiales (p<0.05). Mayor actividad antibiofilm fue observado para CST/ZrO2+CTR en las dos concentraciones, cuando comparados con el grupo control positivo (p<0.05). En conclusión, CTR demostró potencial para promover superior actividad antibiofilm al cemento de silicato tricálcico (CST), sin perjudicar sus propiedades físico-químicas de tiempo de fraguado, pH y solubilidad.
Assuntos
Cimento de Silicato/análise , Placa Dentária , Cetrimônio/análiseRESUMO
OBJECTIVES: This study evaluated 2 nickel-titanium rotary systems and a complementary protocol with an ultrasonic tip and a small-diameter instrument in flattened root canals. MATERIALS AND METHODS: Thirty-two human maxillary second premolars with flattened canals (buccolingual diameter ≥4 times larger than the mesiodistal diameter) at 9 mm from the radiographic apex were selected. The root canals were prepared by ProDesign Logic (PDL) 30/0.01 and 30/0.05 or Hyflex EDM (HEDM) 10/0.05 and 25/0.08 (n = 16), followed by application of the Flatsonic ultrasonic tip in the cervical and middle thirds and a PDL 25/0.03 file in the apical third (FPDL). The teeth were scanned using micro-computed tomography before and after the procedures. The percentage of volume increase, debris, and uninstrumented surface area were analyzed using the Kruskal-Wallis, Dunn, Wilcoxon, analysis of variance/Tukey, and paired and unpaired t-tests (α = 0.05). RESULTS: No significant difference was found in the volume increase and uninstrumented surface area between PDL and HEDM (p > 0.05). PDL had a higher percentage of debris than HEDM in the middle and apical thirds (p < 0.05). The FPDL protocol resulted in less debris and uninstrumented surface area for PDL and HEDM (p < 0.05). This protocol, with HEDM, reduced debris in the middle and apical thirds and uninstrumented surface area in the apical third (p < 0.05). CONCLUSIONS: High percentages of debris and uninstrumented surface area were observed after preparation of flattened root canals. The HEDM, Flatsonic tip, and 25/0.03 instrument protocol enhanced cleaning in flattened root canals.
RESUMO
INTRODUCTION: Calcium silicate-based materials have been proposed as root canal sealers for root canal treatment. The aim of this study was to evaluate the physicochemical properties of a new calcium silicate-based sealer (Bio-C Sealer; Angelus, PR, Brazil) compared with a calcium silicate endodontic sealer (TotalFill BC Sealer; FKG Dentaire SA, La Chaux-de-Fonds, Switzerland) and an epoxy resin sealer (AH Plus; Dentsply DeTrey, Konstanz, Germany). METHODS: The setting time and flow were evaluated based on ISO 6876 standard. The pH value was evaluated after different time intervals of storage in deionized water (1, 7, 14, and 21 days). Radiopacity was evaluated by radiographic analysis in millimeters of aluminum. Solubility and volumetric change were evaluated after 30 days of immersion in distilled water. Solubility was assessed by mass loss (%), and volumetric change was evaluated by micro-computed tomographic imaging. The data were submitted to analysis of variance and Tukey statistical tests (P < .05). RESULTS: TotalFill BC Sealer and Bio-C Sealer were similar regarding radiopacity, volumetric change, and pH values (P > .05). Bio-C Sealer presented the shortest setting time and the highest flow and solubility (P < .05). AH Plus showed the highest radiopacity and the lowest flow, pH, solubility, and volumetric change (P < .05). CONCLUSIONS: Bio-C Sealer showed a short setting time, alkalinization ability, and adequate flow and radiopacity as well as low volumetric change. However, this sealer had higher solubility than the rates required by ISO 6876 standard.