Disposable gold coated pyramidal SERS sensor on the plastic platform.

In this paper we investigate suitability of arrays of gold coated pyramids for surface-enhanced Raman scattering (SERS) sensing applications. Pyramidarrays composed of 1000 nm pit size with 1250 nm pitch lengthwerereplicated on a plastic substrate by roll-to-roll (R2R) ultraviolet (UV) embossing. The level of SERS enhancement, and qualitative performance provided by the new substrate is investigated by comparing Raman spectrum of benzenethiol (BTh) test molecules to the benchmark Klarite SERS substrate which comprises inverted pyramid arrays(1500 nm pit size with 2000 nm pitch length) fabricated on a silicon substrate. The new substrate is found to provide upto 11 times increase in signal in comparison to the inverted pyramid (IV-pyramid) arrays fabricated on an identical plastic substrate. Numerical simulation and experimental evidence suggest that strongly confined electromagnetic fields close to the base of the pyramids, are mainly responsible for the Raman enhancement factor, instead of the fields localized around the tip. Unusually strong plasmon fields are projected upto 200nm from the sidewalls at the base of the pyramid increasing the cross sectional sensing volume.

Disposable plasmonic plastic SERS sensor.

The 'Klarite™' SERS sensor platform consisting of an array of gold coated inverted square pyramids patterned onto a silicon substrate has become the industry standard over the last decade, providing highly reproducible SERS signals. In this paper, we report successful transfer from silicon to plastic base platform of an optimized SERS substrate design which provides 8 times improvement in sensitivity for a Benzenethiol test molecule compared to standard production Klarite. Transfer is achieved using roll-to-roll and sheet-level nanoimprint fabrication techniques. The new generation plastic SERS sensors provide the added benefit of cheap low cost mass-manufacture, and easy disposal. The plastic replicated SERS sensors are shown to provide ~10(7) enhancement factor with good reproducibility (5%).

Probing magnetic order in EELS of chromite spinels using both multiple scattering (FEFF8.2) and DFT (WIEN2k).

The electron energy loss near edge structure on the O K-edge from chromite spinels contains fine structure from the hybridisation of the O p-orbitals and the Cr d-orbitals. Unlike the aluminates, a non-spin polarised calculation of this fine structure differs significantly from experimental observations. This is due to the large magnetic moment on the Cr. Calculations using simplified collinear ordering of the spins and the local spin density approximation give much improved agreement. A real space multiple scattering formalism and a reciprocal space density functional formalism give results in substantial agreement. In general, the actual spin arrangement of these chromites is not known since they are typically frustrated magnetic systems with ordering temperatures in the 10-20K range. The calculations are based on the hypothesis that dynamic short range order persists to room temperature over the time scale of the interaction with the fast electron. However, it is possible that the observed effects are due to the strong paramagnetism present at room temperatures but which it is not possible to simulate accurately at present.