Controlled Individual Skyrmion Nucleation at Artificial Defects Formed by Ion Irradiation.

Magnetic skyrmions are particle-like deformations in a magnetic texture. They have great potential as information carriers in spintronic devices because of their interesting topological properties and favorable motion under spin currents. A new method of nucleating skyrmions at nanoscale defect sites, created in a controlled manner with focused ion beam irradiation, in polycrystalline magnetic multilayer samples with an interfacial Dzyaloshinskii-Moriya interaction, is reported. This new method has three notable advantages: 1) localization of nucleation; 2) stability over a larger range of external field strengths, including stability at zero field; and 3) existence of skyrmions in material systems where, prior to defect fabrication, skyrmions were not previously obtained by field cycling. Additionally, it is observed that the size of defect nucleated skyrmions is uninfluenced by the defect itself-provided that the artificial defects are controlled to be smaller than the inherent skyrmion size. All of these characteristics are expected to be useful toward the goal of realizing a skyrmion-based spintronic device. This phenomenon is studied with a range of transmission electron microscopy techniques to probe quantitatively the magnetic behavior at the defects with applied field and correlate this with the structural impact of the defects.

Quantitative TEM imaging of the magnetostructural and phase transitions in FeRh thin film systems.

Equi-atomic FeRh is a very interesting material as it undergoes a magnetostructural transition from an antiferromagnetic (AF) to a ferromagnetic (FM) phase between 75-105 °C. Its ability to present phase co-existence separated by domain walls (DWs) above room temperature provides immense potential for exploitation of their DW motion in spintronic devices. To be able to effectively control the DWs associated with AF/FM coexistence in FeRh thin films we must fully understand the magnetostructural transition and thermomagnetic behaviour of DWs at a localised scale. Here we present a transmission electron microscopy investigation of the transition in planar FeRh thin-film samples by combining differential phase contrast (DPC) magnetic imaging with in situ heating. We perform quantitative measurements from individual DWs as a function of temperature, showing that FeRh on NiAl exhibits thermomagnetic behaviour consistent with the transition from AF to FM. DPC imaging of an FeRh sample with HF-etched substrate reveals a state of AF/FM co-existence and shows the transition from AF to FM regions proceeds via nucleation of small vortex structures, which then grow by combining with newly nucleated vortex states into larger complex magnetic domains, until it is in a fully-FM state.