RESUMO
In the work here presented, the high performance of ceramic insert tools in milling of ADI 1000 iron casting is analyzed. Austempered ductile irons (ADI) are ductile iron castings with strength and mechanical properties enhanced after specific heat treatment, achieving 1000 MPa or even more. Sintered carbide tools are state of the art in many industrial applications, including iron casting machining, but ceramic inserts are a feasible and promising option since cutting speed can be improved by 5 or even 10 times. A complete testing campaign was performed, starting with coated sintered carbides and aiming at the use of whisker reinforced Al2O3 ceramics and Si3N4 tools. The two most important conclusions are as follows: firstly, that the milling type so-called up-milling (or conventional) is more recommended than down-milling, also known as climb milling, and secondly, that dry machining enhances ceramics performance in comparison with using emulsion coolants (oil in water). Finally, results regarding economic aspects were analyzed based on the tools cost-performance ratio.