The efficient photodegradation of textile dyes is still a challenge, especially considering resistant azo dyes. In this work, zinc/calcium mixed ferrite nanoparticles prepared by the sol-gel method were coupled with silver by a photodeposition method to enhance the photocatalytic potency. The obtained zinc/calcium ferrites are mainly cubic-shaped nanoparticles sized 15 ± 2 nm determined from TEM and XRD and an optical bandgap of 1.6 eV. Magnetic measurements indicate a superparamagnetic behavior with saturation magnetizations of 44.22 emu/g and 27.97 emu/g, respectively, for Zn/Ca ferrite and Zn/Ca ferrite with photodeposited silver. The zinc/calcium ferrite nanoparticles with photodeposited silver showed efficient photodegradation of the textile azo dyes C.I. Reactive Blue 250 and C.I. Reactive Yellow 145. Subsequent cycles of the use of the photocatalyst indicate the possibility of magnetic recovery and reutilization without a significant loss of efficiency.
RESUMO
Magnetic nanoparticles of zinc/calcium ferrite and decorated with silver were prepared by coprecipitation method. The obtained nanoparticles were characterized by UV/Visible absorption, XRD, TEM and SQUID. The mixed zinc/calcium ferrites exhibit an optical band gap of 1.78 eV. HR-TEM imaging showed rectangular nanoplate shapes with sizes of 10 ± 3 nm and aspect ratio mainly between 1 and 1.5. Magnetic measurements indicated a superparamagnetic behavior. XRD diffractograms allowed a size estimation of 4 nm, which was associated with the nanoplate thickness. The silver-decorated zinc/calcium ferrite nanoparticles were successfully employed in the photodegradation of a model dye (Rhodamine B) and industrial textile dyes (CI Reactive Red 195, CI Reactive Blue 250 and CI Reactive Yellow 145). The nanosystems developed exhibited promising results for industrial application in effluent photoremediation using visible light, with the possibility of magnetic recovery.