Elemental Distribution and Structural Characterization of GaN/InGaN Core-Shell Single Nanowires by Hard X-ray Synchrotron Nanoprobes.

Improvements in the spatial resolution of synchrotron-based X-ray probes have reached the nano-scale and they, nowadays, constitute a powerful platform for the study of semiconductor nanostructures and nanodevices that provides high sensitivity without destroying the material. Three complementary hard X-ray synchrotron techniques at the nanoscale have been applied to the study of individual nanowires (NWs) containing non-polar GaN/InGaN multi-quantum-wells. The trace elemental sensitivity of X-ray fluorescence allows one to determine the In concentration of the quantum wells and their inhomogeneities along the NW. It is also possible to rule out any contamination from the gold nanoparticle catalyst employed during the NW growth. X-ray diffraction and X-ray absorption near edge-structure probe long- and short-range order, respectively, and lead us to the conclusion that while the GaN core and barriers are fully relaxed, there is an induced strain in InGaN layers corresponding to a perfect lattice matching with the GaN core. The photoluminescence spectrum of non-polar InGaN quntum wells is affected by strain and the inhomogeneous alloy distribution but still exhibits a reasonable 20% relative internal quantum efficiency.

InGaN/GaN multiple quantum well for fast scintillation application: radioluminescence and photoluminescence study.

We prepare InGaN/GaN multiple quantum well (MQW) structure by metal-organic vapour phase epitaxy and characterize it by fine XRD measurements. We demonstrate its suitability for scintillator application including a unique measurement of wavelength-resolved scintillation response under nanosecond pulse soft x-ray source in extended dynamical and time scales. The photoluminescence and radioluminescence were measured: we have shown that the ratio of the intensity of quantum well (QW) exciton luminescence to the intensity of the yellow luminescence (YL) band IQW/IYL depends strongly on the type and intensity of excitation. Slower scintillation decay measured at YL band maximum confirmed the presence of several radiative recombination centres responsible for wide YL band, which also partially overlap with the QW peak. Further improvements of the structure are suggested, but even the presently reported decay characteristics of the excitonic emission in MQW are better compared to the currently widely used single crystal YAP:Ce or YAG:Ce scintillators. Thus, such a type of a semiconductor scintillator is highly promising for fast detection of soft x-ray and related beam diagnostics.