Screening of hydrogel-based scaffolds for dental pulp regeneration-A systematic review.

OBJECTIVE: The aim of this systematic review was to evaluate the most appropriate hydrogel scaffold type (natural, synthetic or hybrid) to be applied with stem cells for dental pulp regeneration. The findings should help clinicians make an informed choice about the appropriate scaffold to be applied for this approach. DESIGN: Three electronic databases were searched (Medline, Web of Science and Scopus). The review was conducted based on the Preferred Reporting Items for Systematic Reviews and Meta-analysis (PRISMA). RESULTS: From 4990 potentially relevant studies initially identified, 18 papers fulfilled the eligibility criteria and were considered for this review. Natural scaffolds were applied in most studies. Collagen was the most studied scaffold. In 5 of 10 studies, only growth factors were added to the constructs. Even without growth factors, these scaffolds containing stem cells were able to support the formation of dentin. The synthetic scaffolds were the least studied. Only 4 studies were selected, and in 3 of them, the same scaffold (Puramatrix) was evaluated. Puramatrix by itself was unable to form dental pulp when dental pulp stem cells were not present. Synthetic and hybrid hydrogels were unable to attract stem cells from the host. The presence of growth factors in these constructs seems to be of relevance since dental pulp tissue formation was achieved only when the hybrid scaffold was applied with growth factors. CONCLUSION: All types of hydrogel-based scaffolds, when containing mesenchymal stem cells, are able to form connective tissue with different degrees of similarity to dental pulp. However, current data is too heterogeneous to compare and identify the advantages of any specific scaffold.

Residual stress profiles in veneering ceramic on Y-TZP, alumina and ZTA frameworks: measurement by hole-drilling.

OBJECTIVES: The residual stress profile developed within the veneering ceramic during the manufacturing process is an important predicting factor in chipping failures, which constitute a well-known problem with yttria-tetragonal-zirconia polycrystal (Y-TZP) based restorations. The objectives of this study are to measure and to compare the residual stress profile in the veneering ceramic layered on three different polycrystalline ceramic framework materials: Y-TZP, alumina polycrystal (AL) and zirconia toughened alumina (ZTA). METHODS: The stress profile was measured with the hole-drilling method in bilayered disk samples of 19 mm diameter with a 0.7 mm thick Y-TZP, AL or ZTA framework and a 1.5mm thick layer of the corresponding veneering ceramic. RESULTS: The AL samples exhibited increasing compressive stresses with depth, while compressive stresses switching into interior tensile stresses were measured in Y-TZP samples. ZTA samples exhibited compressive stress at the ceramic surface, decreasing with depth up to 0.6mm from the surface, and then becoming compressive again near the framework. SIGNIFICANCE: Y-TZP samples exhibited a less favorable stress profile than those of AL and ZTA samples. Results support the hypothesis of the occurrence of structural changes within the Y-TZP surface in contact with the veneering ceramic to explain the presence of tensile stresses. Even if the presence of Y-TZP in the alumina matrix seems to negatively affect the residual stress profiles in ZTA samples in comparison with AL samples, the registered profiles remain positive in terms of veneer fracture resistance.