Fast, efficient and clean adsorption of bisphenol-A using renewable mesoporous silica nanoparticles from sugarcane waste ash.

Even with all the biological problems associated with bisphenol-A (BPA), this chemical is still being widely used, especially in thermal paper receipts. In this study, renewable mesoporous silica nanoparticles (MSN), obtained from sugarcane ash, functionalized with hexadecyltrimethylammonium (CTAB) were applied as an adsorbent in the removal of BPA from the aqueous solution. The versatility of this material and its BPA adsorption capacity were tested at different pH values, being practically constant at pH between 4 and 9, with a slight increase in pH 10 and a greater increase in pH 11. The removal time evaluation indicates a very fast adsorption process, removing almost 90% of BPA in the first 20 min of contact. The kinetic model indicates a monolayer formation of BPA molecules on the MSN-CTAB surface. The maximum adsorption capacity (Q max) was 155.78 mg g-1, one of the highest found in literature, and the highest for material from a renewable source.

Highly Pure Silica Nanoparticles with High Adsorption Capacity Obtained from Sugarcane Waste Ash.

Silica nanoparticles (SiO2NPs) from renewable sources can be used in very different materials, such as paints, membranes for fuel cells, Li-ion batteries, adsorbents, catalysts, and so on. Brazil is the world's largest producer of sugarcane and generates huge amounts of sugarcane waste ash (SWA), which is a Si-rich source. This study investigates a method to produce highly pure SiO2NPs from SWA. The SiO2NPs were characterized by inductively coupled plasma optical emission spectroscopy, scanning and transmission electron microscopy (TEM), X-ray diffraction analyses, specific surface area and pore distribution, UV and Fourier transform infrared spectroscopy, and thermogravimetric analyses and applied as an adsorbent material in the removal of acid orange 8 (AO8) dye from aqueous solution. The SiO2 content was 88.68 and 99.08 wt % for SWA and SiO2NPs, respectively. TEM images of SWA and SiO2NPs exhibit drastic alterations of the material size ranging from several micrometers to less than 20 nm. The SiO2NPs showed a specific surface area of 131 m2 g-1 and adsorption capacity of around 230 mg g-1 for acid orange 8 dye. Furthermore, the recycling of the SiO2NPs adsorbent after AO8 adsorption was very satisfactory, with reuse for up to five cycles being possible. The results indicate that it was possible to obtain highly pure silica in a nanosize from the waste material and produce an adsorbent with high adsorption capacity and the possibility of reuse.