A Metastable p-Type Semiconductor as a Defect-Tolerant Photoelectrode.

A p-type Cu3Ta7O19 semiconductor was synthesized using a CuCl flux-based approach and investigated for its crystalline structure and photoelectrochemical properties. The semiconductor was found to be metastable, i.e., thermodynamically unstable, and to slowly oxidize at its surfaces upon heating in air, yielding CuO as nano-sized islands. However, the bulk crystalline structure was maintained, with up to 50% Cu(I)-vacancies and a concomitant oxidation of the Cu(I) to Cu(II) cations within the structure. Thermogravimetric and magnetic susceptibility measurements showed the formation of increasing amounts of Cu(II) cations, according to the following reaction: Cu3Ta7O19 + x/2 O2 → Cu(3-x)Ta7O19 + x CuO (surface) (x = 0 to ~0.8). With minor amounts of surface oxidation, the cathodic photocurrents of the polycrystalline films increase significantly, from <0.1 mA cm-2 up to >0.5 mA cm-2, under visible-light irradiation (pH = 6.3; irradiant powder density of ~500 mW cm-2) at an applied bias of -0.6 V vs. SCE. Electronic structure calculations revealed that its defect tolerance arises from the antibonding nature of its valence band edge, with the formation of defect states in resonance with the valence band, rather than as mid-gap states that function as recombination centers. Thus, the metastable Cu(I)-containing semiconductor was demonstrated to possess a high defect tolerance, which facilitates its high cathodic photocurrents.

Nanocatalysis on tailored shape supports: Au and Pd nanoparticles supported on MgO nanocubes and ZnO nanobelts.

Active gold and palladium nanoparticles supported on MgO nanocubes and ZnO nanobelts and transition-metal-containing MgO nanobelts were synthesized by combining evaporation and deposition-precipitation techniques. The high activity and stability of the Au/CeO2 and Pd/CeO2 nanoparticle catalysts deposited on the MgO cubes are remarkable and imply that a variety of efficient catalysts can be designed and tested using this approach. The significant increase in the concentration of corner and edge sites in MgO nanocubes make them well-defined supports to study the detailed mechanism of the catalytic activity enhancement.

Microwave synthesis of supported Au and Pd nanoparticle catalysts for CO oxidation.

We report the microwave synthesis and characterization of Au and Pd nanoparticle catalysts supported on CeO2, CuO, and ZnO nanoparticles for CO oxidation. The results indicate that supported Au/CeO2 catalysts exhibit excellent activity for low-temperature CO oxidation. The Pd/CeO2 catalyst shows a uniform dispersion of Pd nanoparticles with a narrow size distribution within the ceria support. A remarkable enhancement of the catalytic activity is observed and directly correlated with the change in the morphology of the supported catalyst and the efficient dispersion of the active metal on the support achieved by using capping agents during the microwave synthesis. The significance of the current method lies mainly in its simplicity, flexibility, and the control of the different factors that determine the activity of the nanoparticle catalysts.