RESUMO
A High-Throughput Time-Domain ThermoReflectance (HT-TDTR) technique was developed to perform fast thermal conductivity measurements with minimum user actions required. This new setup is based on a heterodyne picosecond thermoreflectance system. The use of two different laser oscillators has been proven to reduce the acquisition time by two orders of magnitude and avoid the experimental artefacts usually induced by moving the elements present in TDTR systems. An amplitude modulation associated to a lock-in detection scheme is included to maintain a high sensitivity to thermal properties. We demonstrate the capabilities of the HT-TDTR setup to perform high-throughput thermal analysis by mapping thermal conductivity and interface resistances of a ternary thin film silicide library FexSiyGe100-x-y (20
RESUMO
We investigate the amorphous structure, chemical bonding, and electrical properties of magnetron sputtered Fe(1-xCx) (0.21 ⩽ x ⩽ 0.72) thin films. X-ray, electron diffraction and transmission electron microscopy show that the Fe(1-xCx) films are amorphous nanocomposites, consisting of a two-phase domain structure with Fe-rich carbidic FeC(y), and a carbon-rich matrix. Pair distribution function analysis indicates a close-range order similar to those of crystalline Fe(3)C carbides in all films with additional graphene-like structures at high carbon content (71.8 at% C). From x-ray photoelectron spectroscopy measurements, we find that the amorphous carbidic phase has a composition of 15-25 at% carbon that slightly increases with total carbon content. X-ray absorption spectra exhibit an increasing number of unoccupied 3d states and a decreasing number of C 2p states as a function of carbon content. These changes signify a systematic redistribution in orbital occupation due to charge-transfer effects at the domain-size-dependent carbide/matrix interfaces. The four-point probe resistivity of the Fe(1-xCx) films increases exponentially with carbon content from â¼200 µΩ cm (x = 0.21) to â¼1200 µΩ cm (x = 0.72), and is found to depend on the total carbon content rather than the composition of the carbide. Our findings open new possibilities for modifying the resistivity of amorphous thin film coatings based on transition metal carbides through the control of amorphous domain structures.
RESUMO
The crystal structure and chemical bonding of magnetron-sputtering deposited nickel carbide Ni1-xCx (0.05 ⩽ x⩽0.62) thin films have been investigated by high-resolution x-ray diffraction, transmission electron microscopy, x-ray photoelectron spectroscopy, Raman spectroscopy, and soft x-ray absorption spectroscopy. By using x-ray as well as electron diffraction, we found carbon-containing hcp-Ni (hcp-NiCy phase), instead of the expected rhombohedral-Ni3C. At low carbon content (4.9 at%), the thin film consists of hcp-NiCy nanocrystallites mixed with a smaller amount of fcc-NiCx. The average grain size is about 10-20 nm. With the increase of carbon content to 16.3 at%, the film contains single-phase hcp-NiCy nanocrystallites with expanded lattice parameters. With a further increase of carbon content to 38 at%, and 62 at%, the films transform to x-ray amorphous materials with hcp-NiCy and fcc-NiCx nanodomain structures in an amorphous carbon-rich matrix. Raman spectra of carbon indicate dominant sp(2) hybridization, consistent with photoelectron spectra that show a decreasing amount of C-Ni phase with increasing carbon content. The Ni 3d-C 2p hybridization in the hexagonal structure gives rise to the salient double-peak structure in Ni 2p soft x-ray absorption spectra at 16.3 at% that changes with carbon content. We also show that the resistivity is not only governed by the amount of carbon, but increases by more than a factor of two when the samples transform from crystalline to amorphous.