Metal release and cell biological compatibility of beta-type Ti-40Nb containing indium.

Small indium (In) additions up to 5 wt % to the beta-type Ti-40Nb alloy effectively improve its mechanical biofunctionality. The impact on its biocompatibility is addressed in this work. Comparative electrochemical polarization studies and inductively coupled plasma optical emission spectrometry analyses were conducted in Tris-buffered saline (on the basis of 150 mM NaCl) with pH 7.6 and 2.0 at 310 ± 1 K with Ti-6Al-4V as reference. The metal ion releases from beta-type alloys were generally very low, for example, those of In3+ ions from (Ti-40Nb)-4In specimens were below 6 × 10-7 mmol/cm2 . X-ray photoelectron spectroscopy revealed the passivation mainly by Ti- and Nb-oxides with traces of In-oxides as the dominating surface process. In vitro studies demonstrate a better human bone marrow stromal cells (hBMSC) activity on the beta-type alloys in comparison to CP-Ti (grade 2), which is mainly due to their high Nb content. At 24 h after seeding on (Ti-40Nb)-4In the metabolic activity of hBMSC was 1.5-fold higher and after 11 days, the tissue non-specific alkaline phosphatase activity was 1.8-fold higher relative to values for CP-Ti. Surface treatments, like chemical etching or plasma oxidation, change the surface topography and the thickness and composition of the oxide layers, but they are not effective in further improving the cell response. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 1686-1697, 2018.

Functionalization of Ti-40Nb implant material with strontium by reactive sputtering.

BACKGROUND: Surface functionalization of orthopedic implants with pharmaceutically active agents is a modern approach to enhance osseointegration in systemically altered bone. A local release of strontium, a verified bone building therapeutic agent, at the fracture site would diminish side effects, which could occur otherwise by oral administration. Strontium surface functionalization of specially designed titanium-niobium (Ti-40Nb) implant alloy would provide an advanced implant system that is mechanically adapted to altered bone with the ability to stimulate bone formation. METHODS: Strontium-containing coatings were prepared by reactive sputtering of strontium chloride (SrCl2) in a self-constructed capacitively coupled radio frequency (RF) plasma reactor. Film morphology, structure and composition were investigated by scanning electron microscopy (SEM), time of flight secondary ion mass spectrometry (ToF-SIMS) and X-ray photoelectron spectroscopy (XPS). High-resolution transmission electron microscopy (HR-TEM) was used for the investigation of thickness and growth direction of the product layer. TEM lamellae were prepared using the focused ion beam (FIB) technique. Bioactivity of the surface coatings was tested by cultivation of primary human osteoblasts and subsequent analysis of cell morphology, viability, proliferation and differentiation. The results are correlated with the amount of strontium that is released from the coating in biomedical buffer solution, quantified by inductively coupled plasma mass spectrometry (ICP-MS). RESULTS: Dense coatings, consisting of SrOxCly, of more than 100 nm thickness and columnar structure, were prepared. TEM images of cross sections clearly show an incoherent but well-structured interface between coating and substrate without any cracks. Sr2+ is released from the SrOxCly coating into physiological solution as proven by ICP-MS analysis. Cell culture studies showed excellent biocompatibility of the functionalized alloy. CONCLUSIONS: Ti-40Nb alloy, a potential orthopedic implant material for osteoporosis patients, could be successfully plasma coated with a dense SrOxCly film. The material performed well in in vitro tests. Nevertheless, the Sr2+ release must be optimized in future work to meet the requirements of an effective drug delivery system.

Controlled surface modification of Ti-40Nb implant alloy by electrochemically assisted inductively coupled RF plasma oxidation.

Low temperature metal oxidation induced by plasma in the absence of liquid electrolytes can be useful for the surface preparation of orthopedic devices since residues from these may be harmful and need to be removed before implantation. In this study the oxidation of Ti-40Nb for biomedical application was achieved by employing an inductively coupled radio frequency oxygen plasma. The correlation between the growth mode of the surface oxide and the electric conductivity ratio of the plasma and the oxide phase were studied by varying the sample temperature, oxygen gas pressure and additional bias potential. The plasma treated samples were characterised by confocal laser microscopy, SEM, EBSD, XPS, TEM and ToF-SIMS. The surface energy was determined by contact angle measurements using the Owens-Wendt-Rabel-Kaelble method. Well adhering oxide layers consisting of TiO2 and Nb2O5 with thicknesses between 50 and 150 nm were obtained. Surface roughness values and microstructure indicate that the growth mode of the oxide can be well controlled by the sample temperature and oxygen gas pressure. At temperatures above 450°C a migration of Ti ions towards the surface controls the growth process. A bias potential higher than +50 V causes rough and defective surfaces with high surface energies.