RESUMO
In this study, the optimal microwave-assisted sol-gel synthesis parameters for achieving TiO2 nanoparticles with the highest specific surface area and photocatalytic activity were determined. Titanium isopropoxide was used as a precursor to prepare the sol (colloidal solution) of TiO2. Isopropanol was used as a solvent; acetylacetone was used as a complexation moderator; and nitric acid was used as a catalyst. Four samples of titanium dioxide were synthesized from the prepared colloidal solution in a microwave reactor at a temperature of 150 °C for 30 min and at a temperature of 200 °C for 10, 20, and 30 min. The phase composition of the TiO2 samples was determined by X-ray diffraction analysis (XRD) and Fourier-transform infrared spectroscopy (FTIR). Nitrogen adsorption/desorption isotherms were used to determine the specific surface area and pore size distributions using the Brunauer-Emmett-Teller (BET) method. The band-gap energy values of the TiO2 samples were determined by diffuse reflectance spectroscopy (DRS). The distribution of Ti and O in the TiO2 samples was determined by SEM-EDS analysis. The effects of adsorption and photocatalytic activity of the prepared TiO2 samples were evaluated by the degradation of ciprofloxacin (CIP) as an emerging organic pollutant (EOP) under UV-A light (365 nm). The results of the photocatalytic activity of the synthesized TiO2 nanoparticles were compared to the benchmark Degussa P25 TiO2. Kinetic parameters of adsorption and photocatalysis were determined and analyzed. It was found that crystalline TiO2 nanoparticles with the highest specific surface area, the lowest energy band gap, and the highest photocatalytic degradation were the samples synthesized at 200 °C for 10 min. The results indicate that CIP degradation by all TiO2 samples prepared at 200 °C show a synergistic effect of adsorption and photocatalytic degradation in the removal process.
RESUMO
The goal of this research is the statistical optimisation of the chemical stability of hybrid microwave-sintered alumina ceramics in nitric acid. The chemical stability of ceramic materials in corrosive media depends on many parameters, such as the chemical and phase composition of the ceramics, the properties of the aggressive medium (concentration, temperature, and pressure), and the exposure time. Therefore, the chemical stability of alumina ceramics in different aqueous nitric acid solution concentrations (0.50 mol dm-3, 1.25 mol dm-3, and 2.00 mol dm-3), different exposure times (up to 10 days), as well as different temperatures (25, 40, and 55 °C), was investigated, modelled, and optimised. The chemical stability of high purity alumina ceramics (99.8345 wt.% of Al2O3) was determined by measuring the amount of eluted ions (Al3+, Ca2+, Fe3+, Mg2+, Na+, and Si4+) obtained by inductively coupled plasma atomic emission spectrometry. The changes in the density of alumina ceramics during the chemical stability monitoring were also determined. The Box-Behnken approach was employed to reach the optimum conditions for obtaining the highest possible chemical stability of alumina at a given temperature range, exposure time, and molar concentration of nitric acid. It was found that an increase in exposure time, temperature, and nitric acid concentration led to an increase in the elution of ions from hybrid microwave-sintered alumina. Higher amounts of eluted ions, Al3+ (14.805 µg cm-2), Ca2+ (7.079 µg cm-2), Fe3+ (0.361 µg cm-2), Mg2+ (3.654 µg cm-2), and Na+ ions (13.261 µg cm-2), were obtained at 55 °C in the 2 mol dm- 3 nitric acid. The amount of eluted Si4+ ions is below the detection limit of inductively coupled plasma atomic emission spectrometry. The change in the alumina ceramic density during the corrosion test was negligible.
