Fiber orientation of the transverse carpal ligament.

The transverse carpal ligament is the volar roof of the carpal tunnel. Gross observation shows that the ligament appears to have fibers that roughly orient in the transverse direction. A closer anatomical examination shows that the ligament also has oblique fibers. Knowledge of the fiber orientation of the transverse carpal ligament is valuable for further understanding the ligament's role in regulating the structural function of the carpal tunnel. The purpose of this study is to quantify collagen fiber orientation within the transverse carpal ligament using the small angle light scattering technique. Eight transverse carpal ligament samples from cadaver hands were used in this study. Individual 20-µm sections were cut evenly along the thickness of the transverse carpal ligament. Sections of three thickness levels (25%, 50%, and 75% from the volar surface) were collected for each transverse carpal ligament. Fibers were grouped in the following orientation ranges: transverse, longitudinal, oblique in the pisiform-trapezium (PT), and oblique in the scaphoid-hamate (SH) directions. In analyzing the fiber percentages, the orientation types for the different thickness levels of the ligament showed that the transverse fibers were the most prominent (>60.7%) followed by the PT oblique (18.6%), SH oblique (13.0%), and longitudinal (8.6%) fibers.

Fixation of vascular grafts with increased glutaraldehyde concentration enhances mechanical properties without increasing calcification.

Our objective was to study the effect of glutaraldehyde (GLU) concentration, heat, and photooxidation on mechanical properties and calcification of bovine pericardium grafts in an in vivo model. Fresh pericardia were treated as follows: 0.625% GLU for 7 days (standard); 0.625%, 1%, and 3% GLU at 4 degrees C for 20 days and 50 degrees C for additional 20 days; irradiation in cross-linking medium with metilene blue at 0 degrees C for 8 hours. Tissues were subjected to tensile mechanical tests (n = 76). Fixed patches were subcutaneously implanted in mice for 50 days (n = 16 per treatment). Calcification was assessed by atomic absorption spectrophotometry (n = 55) and von Kossa staining (n = 28). Analysis of variance and Tukey's test were used for statistical analysis. The 3% GLU and 3% GLU + heat treatments showed an enhancement of the mechanical properties above standard treatment. No significant difference was found in calcification between treatments. The 3% GLU treatment enhances the mechanical properties of the tissue above standard treatment without increasing calcification and without applying heat; therefore it is recommended for high-strength applications. Supplementary treatments to decrease calcification could be combined with this methodology to obtain a high-strength-low-calcification biomaterial for manufacturing of long-term cardiovascular grafts.