We report the molecular beam epitaxy (MBE) growth and properties of (MgSe)n(ZnxCd1-x Se)m short-period superlattices(SPSLs) for potential application in II-VI devices grown on InP substrates. SPSL structures up to 1 µm thick with effective bandgaps ranging from 2.6 eV to above 3.42 eV are grown and characterized, extending the typical range possible for the ZnxCdyMg1-x-ySe random alloy beyond 3.2 eV. Additionally, ZnxCd1-xSe single and multiple quantum well structures using the SPSL barriers are also grown and investigated. The structures are characterized utilizing reflection high-energy electron diffraction, X-ray reflectance, X-ray diffraction and photoluminescence. We observed layer-by-layer growth and smoother interfaces in the QWs grown with SPSL when compared to the ZnxCdyMg1-x-ySe random alloy. The results indicate that this materials platform is a good candidate to replace the random alloy in wide bandgap device applications.
RESUMO
We present the growth and characterization of ZnCdSe/ZnCdMgSe quantum cascade (QC) heterostructures grown by molecular beam epitaxy (MBE) and designed to operate at 6-8µm. These structures utilize the better-understood ZnCdMgSe with InP lattice matched compositions yielding a bandgap of 2.80 eV as compared to previous work which used ZnCdMgSe compositions with bandgaps at 3.00 eV. Grown structures posses good structural and optical properties evidenced in X-ray diffraction and photoluminescence studies. Fabricated mesa devices show temperature dependent I-V measurements with differential resistance of 3.6 Ω, and a turn on voltage of 11V consistent with design specifications. Electroluminescence was observed in these devices up to room temperature with emission centered at 7.1 µm and line widths of â¼16%(ΔE/E) at 80K. The results show that these are well-behaved electroluminescent structures. Addition of waveguide layers and further improvements in well barrier interfaces are being pursued in efforts to demonstrate lasing.