Three-dimensional (3D) printing is a very flexible process to design various objects of original shapes. Previous works highlighted the preparation of new multimaterials composed of an original sandwich structure made of the ethylene vinyl acetate copolymer containing 30 wt % of aluminum trihydroxide in which a hydrogel phase made of agar and vermiculite was incorporated. This original material revealed an extremely low heat release rate (HRR) (with a reduction of 86 and 64% with regard to the peak of the HRR and total heat release, respectively, when compared to the same sample without hydrogel filling) during its heat exposure at 50 kW/m2 according to the mass loss cone calorimetry test. However, the time to ignition (TTI) of this material was not improved. This work consequently focuses on delaying the time to ignition of this hydrogel sandwich 3D-printed multimaterial. Solution consists in depositing by pulsed DC magnetron sputtering a low-emissivity thin coating on the exposed skin surface. This coating reflects most of the infrared rays responsible for heat absorption and thus delays the ignition of the underlying material. The thermal resistance performances of this coated sandwich 3D-printed multimaterial were evaluated, and a mechanism of action was proposed to explain the dramatic enhancement of the properties.

Intumescent Polymer Metal Laminates for Fire Protection.

Intumescent paints are applied on materials to protect them against fire, but the development of novel chemistries has reached some limits. Recently, the concept of "Polymer Metal Laminates," consisting of alternating thin aluminum foils and thin epoxy resin layers has been proven efficient against fire, due to the delamination between layers during burning. In this paper, both concepts were considered to design "Intumescent Polymer Metal Laminates" (IPML), i.e., successive thin layers of aluminum foils and intumescent coatings. Three different intumescent coatings were selected to prepare ten-plies IPML glued onto steel substrates. The IPMLs were characterized using optical microscopy, and their efficiency towards fire was evaluated using a burn-through test. Thermal profiles obtained were compared to those obtained for a monolayer of intumescent paint. For two of three coatings, the use of IPML revealed a clear improvement at the beginning of the test, with the slopes of the curves being dramatically decreased. Characterizations (expansion measurements, microscopic analyses, in situ temperature, and thermal measurements) were carried out on the different samples. It is suggested that the polymer metal laminates (PML) design, delays the carbonization of the residue. This work highlighted that design is as important as the chemistry of the formulation, to obtain an effective fire barrier.