This work presents a novel approach to producing water soluble manganese-doped core/shell ZnS/ZnS quantum dots (ZnS:Mn/ZnS). The Mn-doped ZnS core was prepared through a nucleation doping strategy and a ZnS shell was grown on ZnS:Mn d-dots by decomposition of Zn(2+)-3-mercaptopropionic acid (MPA) complexes at 100 °C. It was found that the Mn2+(4)T1â6A1 fluorescence emission at â¼590 nm significantly increased after growth of the shell when the Mn2+ doping content was 4.0 at.%. A photoluminescence quantum yield of â¼22% was obtained for core/shell nanocrystals. The nanoparticles were structurally and compositionally characterized by transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, and dynamic light scattering. The surface MPA molecules favor the dispersion of ZnS:Mn/ZnS QDs in aqueous media and make possible conjugation with targeting folic acid molecules. The folate receptor-mediated delivery of folic acid-conjugated ZnS:Mn/ZnS QDs was demonstrated using confocal microscopy with biphotonic excitation. Bare and folate-conjugated QDs exhibit only weak cytotoxicity towards folate receptor-positive T47D cancer cells and MCF-7 cells, used as a reference, at high concentrations (mmolar range) after 72h incubation.
Assuntos
Corantes Fluorescentes/química , Ácido Fólico/química , Magnésio/química , Neoplasias/patologia , Pontos Quânticos , Sulfetos/química , Compostos de Zinco/química , Linhagem Celular Tumoral , Humanos , Microscopia Confocal , Microscopia Eletrônica de Transmissão , Espectrometria de Fluorescência , Espectrofotometria Ultravioleta , Difração de Raios XRESUMO
Relatively monodisperse and highly luminescent Mn(2+)-doped zinc blende ZnSe nanocrystals were synthesized in aqueous solution at 100 °C using the nucleation-doping strategy. The effects of the experimental conditions and of the ligand on the synthesis of nanocrystals were investigated systematically. It was found that there were significant effects of molar ratio of precursors and heating time on the optical properties of ZnSe:Mn nanocrystals. Using 3-mercaptopropionic acid as capping ligand afforded 3.1 nm wide ZnSe:Mn quantum dots (QDs) with very low surface defect density and which exhibited the Mn(2+)-related orange luminescence. The post-preparative introduction of a ZnS shell at the surface of the Mn(2+)-doped ZnSe QDs improved their photoluminescence properties, resulting in stronger emission. A 2.5-fold increase in photoluminescence quantum yield (from 3.5 to 9%) and of Mn(2+) ion emission lifetime (from 0.62 to 1.39 ms) have been observed after surface passivation. The size and the structure of these QDs were also corroborated by using transmission electron microscopy, energy dispersive spectroscopy, and X-ray powder diffraction.