Cohesive Zone Modeling of the Interface Fracture in Full-Thermoplastic Hybrid Composites for Lightweight Application.

With the increasing demand for lightweight and high-performance materials in the automotive and aerospace industries, full-thermoplastic hybrid composites have emerged as a pivotal solution, offering enhanced mechanical properties and design flexibility. This work aims to numerically model the fracture strength in full-thermoplastic hybrid composites made by forming and overmolding organosheets. The mode I fracture was investigated by modeling the behavior of T-joint specimens under a tensile test following the cohesive zone modeling (CZM) approach. The sample was designed to replicate the connection between the laminate and the overmolded part. Double cantilever beam (DCB) specimens were manufactured with organosheets and tested to mode I opening to determine the interlaminar fracture toughness. The fracture toughness out of the mode I test with DCB specimens was used to define the CZM parameters that describe the traction-separation law. Later, due to the particular geometry of the T-join specimens that under tensile load work close to pure mode I, the cohesive parameters were determined by inverse analysis, i.e., calibrating the theoretical models to match experimental results. The fracture resistance T-joint specimens appeared dependent on the fiber-bridging phenomenon during the delamination. In particular, the presence of fiber-bridging visible from the experimental results has been replicated by virtual analyses, and it is observed that it leads to a higher energy value before the interface's complete breakage. Moreover, a correspondence between the mode I fracture toughness of the DCB specimen and T-joint specimens was observed.

Modeling the Adhesion Bonding Strength in Injection Overmolding of Polypropylene Parts.

In this work, the bonding strength of overmolded polypropylene is investigated and modeled. A T-joint specimen was designed to replicate the bonding between a base and an overmolded stem made of the same polymer: a previously molded plaque was used for the base, and the stem was directly overmolded. The effect of melt temperature, holding pressure, and localized heating was investigated following the design of experiments approach. Both the melt and base temperature positively affect the welding strength. On the contrary, the holding pressure negatively contributed, as the crystallization temperature significantly increases with pressure. Then, the bonding strength of the specimens was predicted using a non-isothermal healing model. Moreover, the quadratic distance of diffusion (based on the self-diffusion model) was calculated and correlated with the bonding strength prediction. The non-isothermal healing model well predicts the bonding strength when the reptation time is calculated within the first 0.09 s of the interface temperature evolution. The prediction error ranges from 1% to 35% for the specimens overmolded at high and low melt and base temperatures, respectively.