Assessing the Rheological, Mechanical, and Photocatalytic Properties of Niobium Oxide-Incorporated White Cement Pastes.

Niobium oxide (Nb2O5) is a semiconductor that exhibits photocatalytic properties, making it potentially valuable in addressing air pollution, self-cleaning, and self-disinfection in cement-based materials (CBMs). Therefore, this study aimed to evaluate the impact of different Nb2O5 concentrations on various parameters, including rheological characteristics, hydration kinetics (measured using isothermal calorimetry), compressive strength, and photocatalytic activity, specifically in the degradation of Rhodamine B (RhB) in white Portland cement pastes. The incorporation of Nb2O5 increased the yield stress and viscosity of the pastes by up to 88.9% and 33.5%, respectively, primarily due to the larger specific surface area (SSA) provided by Nb2O5. However, this addition did not significantly affect the hydration kinetics or the compressive strength of the cement pastes after 3 and 28 days. Tests focusing on the degradation of RhB in the cement pastes revealed that the inclusion of 2.0 wt.% of Nb2O5 was insufficient to degrade the dye when exposed to 393 nm UV light. However, an interesting observation was made concerning RhB in the presence of CBMs, as it demonstrated a degradation mechanism that was not dependent on light. This phenomenon was attributed to the production of superoxide anion radicals resulting from the interaction between the alkaline medium and hydrogen peroxide.

Evaluation of CNTs and SiC Whiskers Effect on the Rheology and Mechanical Performance of Metakaolin-Based Geopolymers.

Despite geopolymers having emerged as a more sustainable alternative to Portland cement, their rheological properties still need to be thoroughly investigated, aiming at the material's applicability. Additionally, studies that evaluated the fresh state of geopolymer composites with nanomaterials are scarce. Thus, two metakaolin-based geopolymer systems were reinforced with nanomaterials with a similar geometry: carbon nanotubes (CNT) and silicon carbide whiskers (SCW). The nanomaterials incorporation was assessed by rotational rheometry (conducted up to 110 min), isothermal calorimetry, compressive strength after 7 and 28 days, and the microstructure was investigated using X-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FTIR). CNT and SCW incorporation (0.20 wt.%) did not significantly affect the yield stress and viscosity of the R2-group (based on metakaolin type 2), while increasing the rheological parameters up to 56.0% for the R1-group (based on metakaolin type 1). Both additions modified the reaction kinetics. Increments of up to 40.7% were observed in the compressive strength of geopolymer pastes with the incorporation of a SCW content of 0.2 wt.%. XRD and FTIR results suggest similar structural modifications between precursors. Nevertheless, R2 showed substantial transformations while the R1 group exhibited anhydrous material that can react over time. Overall, incorporating CNT and SCW contributed to higher mechanical increments on systems with average mechanical strength (R1) compared to systems with higher potential mechanical performance (R2).

Influence of Ultrasonication of Functionalized Carbon Nanotubes on the Rheology, Hydration, and Compressive Strength of Portland Cement Pastes.

The functionalization process usually increases the localized defects of carbon nanotubes (CNT). Thus, the ultrasonication parameters used for dispersing non-functionalized CNT should be carefully evaluated to verify if they are adequate in dispersing functionalized CNT. Although ultrasonication is widely used for non-functionalized CNT, the effect of this dispersing process of functionalized CNT has not been thoroughly investigated. Thus, this work investigated the effect of ultrasonication on functionalized CNT + superplasticizer (SP) aqueous dispersions by ultraviolet-visible (UV-Vis) spectroscopy, dynamic light scattering (DLS), and Fourier transform infrared spectroscopy (FTIR). Furthermore, Portland cement pastes with additions of 0.05% and 0.1% CNT by cement weight and ultrasonication amplitudes of 0%, 50% and 80% were evaluated through rheometry, isothermal calorimetry, compressive strength at 1, 7 and 28 days, X-ray diffraction (XRD), and thermogravimetric analysis (TGA). FTIR results from CNT + SP dispersions indicated that ultrasonication may negatively affect SP molecules and CNT graphene structure. The increase in CNT content and amplitude of ultrasonication gradually increased the static and dynamic yield stress of paste but did not significantly affect its hydration kinetics. Compressive strength results indicated that the optimum CNT content was 0.05% by cement weight, which increased the strength of composite by up to 15.8% compared with the plain paste. CNT ultrasonication neither increases the degree of hydration of cement nor the mechanical performance of composite when compared with mixes containing unsonicated CNT. Overall, ultrasonication of functionalized CNT is not efficient in improving the fresh and hardened performance of cementitious composites.

Utilization of Thermally Treated SiC Nanowhiskers and Superplasticizer for Cementitious Composite Production.

Nanomaterials are potential candidates to improve the mechanical properties and durability of cementitious composites. SiC nanowhiskers (NWs) present exceptional mechanical properties and have already been successfully incorporated into different matrices. In this study, cementitious composites were produced with a superplasticizer (SP) and 0-1.0 wt % SiC NWs. Two different NWs were used: untreated (NT-NW) and thermally treated at 500 °C (500-NW). The rheological properties, cement hydration, mechanical properties, and microstructure were evaluated. The results showed that NWs incorporation statistically increased the yield stress of cement paste (by up to 10%) while it led to marginal effects in viscosity. NWs enhanced the early cement hydration, increasing the main heat flow peak. NWs incorporation increased the compressive strength, tensile strength, and thermal conductivity of composites by up to 56%, 66%, and 80%, respectively, while it did not statistically affect the water absorption. Scanning electron microscopy showed a good bond between NWs and cement matrix in addition to the bridging of cracks. Overall, the thermal treatment increased the specific surface area of NWs enhancing their effects on cement properties, while SP improved the NWs dispersion, increasing their beneficial effects on the hardened properties.