Solution Blow Spun Silica Nanofibers: Influence of Polymeric Additives on the Physical Properties and Dye Adsorption Capacity.

The physical properties of porous silica nanofibers are an important factor that impacts their performance in various applications. In this study, porous silica nanofibers were produced via solution blow spinning (SBS) from a silica precursor/polymer solution. Two polyvinylpyrrolidone (PVP, Mw = 360,000 and 1,300,000) were chosen as spinning aids in order to create different pore properties. The effect of their physical properties on the adsorption of methylene blue (MB) in an aqueous solution was explored. After forming, the nanofibers were calcined to remove the organic phase and create pores. The calcined nanofibers had a large amount of micro and mesopores without the use of additional surfactants. The molecular weight of the PVP impacted the growth of silica particles and consequently the pore size. High Mw PVP inhibited the growth of silica particles, resulting in a large volume of micropores. On the other hand, silica nanofibers with a high fraction of mesopores were obtained using the lower Mw PVP. These results demonstrate a simple method of producing blow spun silica nanofibers with defined variations of pore sizes by varying only the molecular weight of the PVP. In the adsorption process, the accessible mesopores improved the adsorption performance of large MB molecules.

Solution blow spun nanocomposites of poly(lactic acid)/cellulose nanocrystals from Eucalyptus kraft pulp.

Cellulose nanocrystals (CNCs) were extracted from Eucalyptus kraft pulp by sulfuric acid hydrolysis, and esterified with maleic anhydride (CNCMA). The incorporation of sulfate ester groups on the cellulose surface resulted in higher stability of the nanoparticles in aqueous suspensions and lower thermal stability. Then, PLA/CNC and PLA/CNCMA nanocomposites were successfully obtained by solution blow spinning (SBS) using dimethyl carbonate (DMC) as solvent. CNC and CNCMA indicated to be acting both as nucleating agents or growth inhibitors of PLA crystal and tends to favor the formation of PLA crystals of higher stability. A fraction of the nanocrystals indicate to be exposed on the surface of the PLA fibers, since the hydrophilicity of the composite films increased significantly. Such composites may have potential application as filtering membranes or adsorbents.