Sensitive and selective detection of trivalent chromium using Hyper Rayleigh Scattering with 5,5'-dithio-bis-(2-nitrobenzoic acid)-modified gold nanoparticles.

Hyper Rayleigh Scattering (HRS) and absorption spectral assays using surface-modified gold nanoparticles (AuNP) have been developed for sensitive and selective detection of trivalent chromium (Cr3+) from other metal ions including hexavalent chromium (as Cr2O72-). Gold nanoparticles of 13 nm, covalently attached with 5,5'-dithio-bis-(2-nitrobenzoic acid) (AuNP-DTNBA), is used as a probe for both the absorption and HRS assays. AuNP-DTNBA is able to detect Cr3+ at 20 ppb level at pH 6.0 using absorption spectral change of the AuNP-DTNBA. Visible color change can be observed when mixed with 250 ppb of Cr3+, while there is no color change when mixed with 2 ppm level of some of the most common metal ions such as Cr2O72-, Hg2+, Ba2+, Fe3+, Pb2+, Na+, Zn2+, Cd2+, Co2+, Mn2+, Ca2+, and Ni2+. However, a color change is observed when mixed with Ni2+, Zn2+, and Cd2+ at a concentration higher than 2 ppm. The detection limit for the HRS assay is on a remarkable 25 ppt level, and there is no detectable HRS signal at 2 ppm level for Cr2O72-, Hg2+, Ba2+, Fe3+, Pb2+, Na+, Zn2+, Cd2+, Co2+, Mn2+, Ca2+, and Ni2+.

Synergistic effect of PVP and PEG on the behavior of silver nanoparticle-polymer composites.

Silver nanoparticles-polymer nanocomposites, Ag-(1 - x)PVP-(x)PEG, were synthesized by wet chemical method in the presence of polyvinylpyrrolidone (PVP) and polyethylene glycol (PEG). A mixture of two stabilizing agent PVP and PEG is found to play a crucial role in controlling the morphology of nanocrystalline silver particles in the composite. This is inferred based on the shape and size study of nanocrystalline silver using the X-ray diffraction, transmission electron microscopy, Uv-vis spectroscopy, FTIR, and surface enhance Raman studies. These results suggest asymmetrical growth of silver nanocrystalline particles in the presence of both PVP and PEG. Comparison of the thermal properties of the Ag-polymer nanocomposites with pure polymers, PVP and PEG, showed that the thermal stability of the nanocomposite deteriorates by as much as 75 degrees C in the presence of low PEG concentration (x < or = 0.6) and improves by around 45 degrees C at higher PEG concentration (x > 0.6). The study highlight the fact that the morphology of nanocrystalline silver can be altered just by varying the polymer weight ratios rather than any processing parameters, thus offering a novel, simple, and controlled synthesis engineering route to the formation of nanocrystalline silver in polymer matrix.