Direct observation of lithium metal dendrites with ceramic solid electrolyte.

Dendrite formation, which could cause a battery short circuit, occurs in batteries that contain lithium metal anodes. In order to suppress dendrite growth, the use of electrolytes with a high shear modulus is suggested as an ionic conductive separator in batteries. One promising candidate for this application is Li7La3Zr2O12 (LLZO) because it has excellent mechanical properties and chemical stability. In this work, in situ scanning electron microscopy (SEM) technique was employed to monitor the interface behavior between lithium metal and LLZO electrolyte during cycling with pressure. Using the obtained SEM images, videos were created that show the inhomogeneous dissolution and deposition of lithium, which induce dendrite growth. The energy dispersive spectroscopy analyses of dendrites indicate the presence of Li, C, and O elements. Moreover, the cross-section mapping comparison of the LLZO shows the inhomogeneous distribution of La, Zr, and C after cycling that was caused by lithium loss near the Li electrode and possible side reactions. This work demonstrates the morphological and chemical evolution that occurs during cycling in a symmetrical Li-Li cell that contains LLZO. Although the superior mechanical properties of LLZO make it an excellent electrolyte candidate for batteries, the further improvement of the electrochemical stabilization of the garnet-lithium metal interface is suggested.

In-Situ Characterization of Lithium Native Passivation Layer in A High Vacuum Scanning Electron Microscope.

A technique to characterize the native passivation layer (NPL) on pure lithium metal foils in a scanning electron microscope (SEM) is described in this paper. Lithium is a very reactive metal, and consequently, observing and quantifying its properties in a SEM is often compromised by rapid oxidation. In this work, a pure lithium energy-dispersive x-ray spectrum is obtained for the first time in a high vacuum SEM using a cold stage/cold trap with liquid nitrogen reservoir outside the SEM chamber. A nanomanipulator (OmniProbe 400) inside the microscope combined with x-ray microanalysis and windowless energy dispersive spectrometer is used to fully characterize the NPL of lithium metal and some of its alloys by a mechanical removal procedure. The results show that the native films of pure lithium and its alloys are composed of a thin (25 nm) outer layer that is carbon-rich and an inner layer containing a significant amount of oxygen. Differences in thickness between laminated and extruded samples are observed and vary depending on the alloy composition.

In Situ Scanning Electron Microscopy Detection of Carbide Nature of Dendrites in Li-Polymer Batteries.

Li metal batteries suffer from dendrite formation which causes short circuit of the battery. Therefore, it is important to understand the chemical composition and growth mechanism of dendrites that limit battery efficiency and cycle life. In this study, in situ scanning electron microscopy was employed to monitor the cycling behavior of all-solid Li metal batteries with LiFePO4 cathodes. Chemical analyses of the dendrites were conducted using a windowless energy dispersive spectroscopy detector, which showed that the dendrites are not metallic lithium as universally recognized. Our results revealed the carbide nature of the dendrites with a hollow morphology and hardness greater than that of pure lithium. These carbide-based dendrites were able to perforate through the polymer, which was confirmed by milling the polymer using focused ion beam. It was also shown that applying pressure on the battery can suppress growth of the dendrites.