RESUMO
Two Ce-Zr-La/Al2O3 composite oxides, CZLA-C and CZLA-B, were synthesized using a co-precipitation method in a continuous stirred-tank reactor (CSTR) and a batch reactor (BR), respectively. Two Rh-based three-way catalysts (TWCs), Rh/CZLA-C and Rh/CZLA-B were obtained by a wet-impregnation method using the two composites as the supports. The physicochemical properties of the samples before and after thermal treatment at 1000 °C were characterized by N2 adsorption-desorption, X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), H2-temperature programmed reduction (H2-TPR) and CO chemisorption. The results indicated that CZLA-C shows higher thermal stability than CZLA-B due to a sparsely-agglomerated morphology. Compared with Rh/CZLA-B, Rh/CZLA-C displayed better reducibility and higher thermal stability and exhibited significantly higher activity in the catalytic removal of the simulated gasoline vehicle exhaust emission (NO, CO and C3H8). Our work can provide a facile and economical synthesis route to advanced support materials and catalysts for exhaust emission control.
RESUMO
Five monolithic catalysts with low noble metal content were prepared by immerge method (Pt/gamma-Al2O3, Pt/La-Al2O3, Pt/YSZ-Al2O3, Pt+Pd/La-Al2O3 and Pd/La-Al2O3) and their activity measurements were carried out in a conventional fixed-bed flow reactor. The results show that La-Al2O3 can promote activity of the prepared catalysts and can decrease the complete conversion temperature of cooking fume. The Pt/La-Al2O3 catalyst has the highest activity and can be applied in wide range of gas hourly space velocity (GHSV). Some characterizations (XRD, TPR) were carried out with the objective to explain differences in catalytic behaviors. The prepared catalyst showed a great potential for application.