Interlocking Evaluation of Mesoscopic Skeleton with the Compaction Degree of Hot-Mix Asphalt.

Asphalt mixtures are multi-phase composites composed of aggregates, bitumen, mineral powders, and voids, and various structures are intertwined during the compaction process. Most of the traditional research focuses on the macro-scale domain, and it is difficult to obtain the internal structure of asphalt mixture in different compaction processes. With the continuous development of digital image technology, the influence of the meso-structure of the asphalt mixture on the compaction quality of the asphalt mixture has become a new means to evaluate the performance of the asphalt mixture. In this paper, different numbers of compactions are selected to represent different stages in the compaction process, the digital images of specimens in different compaction stages are obtained by industrial CT scanning technology. Then, the images are processed and reconstructed in three dimensions using improved image segmentation methods, and the position characteristics and geometric information of coarse aggregate are obtained by combining the Oriented Bounding Box (OBB). The meso-response characteristics of the skeleton structure of the asphalt mixture during compaction were studied. The influence of the internal structure of the mixture on the compaction quality of the mixture was obtained, which is of great significance for the study of improving the durability of the pavement. The results show that the "effective coordination number" (the number of aggregate particles that can transmit force in the skeleton structure) is greatly related to the aggregate size. With the compaction process, the centroid of coarse aggregate in the upper layer of the specimen reflects the overall downward movement trend. The inclination angle of the aggregate spindle tends to be in the range of 80°~100°; the anisotropic amplitude of the xy plane increases, and the direction of the aggregate spindle becomes more and more consistent. With the increase in the number of rotational compactions, these four parameters showed obvious rules, indicating that this meso-characteristic index could well characterize the compaction quality of the asphalt mixture in the compaction process.

Geometrical Optimization and Transverse Thermoelectric Performances of Fe/Bi2Te2.7Se0.3 Artificially Tilted Multilayer Thermoelectric Devices.

Transverse thermoelectric performance of the artificially tilted multilayer thermoelectric device (ATMTD) is very difficult to be optimized, due to the large degree freedom in device design. Herein, an ATMTD with Fe and Bi2Te2.7Se0.3 (BTS) materials was proposed and fabricated. Through high-throughput calculation of Fe/BTS ATMTD, a maximum of calculated transverse thermoelectric figure of merit of 0.15 was obtained at a thickness ratio of 0.49 and a tilted angle of 14°. For fabricated ATMTD, the whole Fe/BTS interface is closely connected with a slight interfacial reaction. The optimizing Fe/BTS ATMTD with 12 mm in length, 6 mm in width and 4 mm in height has a maximum output power of 3.87 mW under a temperature difference of 39.6 K. Moreover the related power density per heat-transfer area reaches 53.75 W·m-2. This work demonstrates the performance of Fe/BTS ATMTD, allowing a better understanding of the potential in micro-scaled devices.

Study on pollution characteristics of urban pavement runoff.

Urban pavement runoff has become an important pollution source endangering the quality of urban water. This paper analyzed the characteristics of particle size distribution of road-deposited sediment (RDS). The variation of pollutants with RDS content is presented. Based on continuous sampling of runoff, the variation between pollutant concentration and rainfall characteristics is revealed. The results show that each particle group shares similar content except for the group smaller than 0.075 mm. However, the smaller particles have a stronger ability to adsorb heavy metals (Zn, Pb, Cu), and a weaker ability to adsorb chemical oxygen demand (COD). The concentrations of different pollutants have different relationships with rainfall and runoff time. The concentration of suspended solids (SS) decreases steadily with runoff time, while the concentration of heavy metals increases first and then decreases. The first 30 minutes of runoff is the best time to treat heavy metals and SS. The five-day biochemical oxygen demand (BOD5) and total petroleum hydrocarbons (TPHs) concentration are mainly affected by rainfall intensity. The result presented in this paper may provide a useful reference for the treatment of pavement runoff pollution.

Resistance to Ultraviolet Aging of Nano-SiO2 and Rubber Powder Compound Modified Asphalt.

Ultraviolet (UV) aging degrades the life span of asphalt pavement, nanomaterials used as modifiers exhibit good shielding function on UV light, but generally degrade the low-temperature property of asphalt, a compound modification was found to be a solution. In this study, nano-SiO2 and rubber powder were blended together with base asphalt to prepare compound modified asphalt. Compound modified asphalt with different blending dosages were subjected to UV light via a self-made UV aging simulation chamber. Basic performance tests and rheological tests were conducted including the UV aging influence. An optimum compound ratio was finally recommended based on the goal to remove the adverse effect of nano-SiO2 on the thermal cracking. Results show that the anti-UV aging property of asphalt is improved obviously due to the blocking function of nano-SiO2 and carbon black in rubber powder, and the enhancing effect of nano-SiO2 is found to be the most significant.

The NOx Degradation Performance of Nano-TiO2 Coating for Asphalt Pavement.

The NOx degradation performance of nano-TiO2 as a coating material for the road environment was evaluated in this research. The nano-TiO2 coating materials for both road surface and roadside were prepared by using anatase nano-TiO2, activated carbon powder, silane coupling agent and deionized water. The impact of varying amounts of coating material and silane coupling agent were evaluated. The road environment of NOx degradation was simulated by the photocatalytic test system designed by the research team. For the road surface coating, the photocatalytic degradation experiments of NO under different radiation intensities were carried out. The results show that the material has good photocatalytic degradation performance, and the proper amount of silane coupling agent can enhance the bonding performance of the material and asphalt mixture. For the roadside coating, sodium dodecylbenzene sulfonate was selected as the surfactant to carry out the photocatalytic degradation experiment of NO2 with different dosages of surfactant. The results showed that when the mass ratio of nano-TiO2 and surfactant was about 1:2, the catalytic degradation effect of the material was the best.

Examination of Poly (Styrene-Butadiene-Styrene)-Modified Asphalt Performance in Bonding Modified Aggregates Using Parallel Plates Method.

Although asphalt-aggregate bonding provides contacting strength for hot mix asphalt (HMA), it is still ignorant in dynamic shear test, due to the only use of metal parallel plate. Modified parallel plates cored from different types of aggregate were provided to simulate aggregate-asphalt-aggregate (AAA) sandwich in HMA, aiming at the comprehensive interpretation on bonding's influence. This study began with an experimental design, aggregate plates, and joint clamps were processed to be installed into the rheometer. Aggregate type and loading conditions were set as essential variables. Subsequently, microscopic tests were utilized to obtain chemical components of aggregate, micro morphology of interface, and roughness of plates. The shearing tests for poly (styrene-butadiene-styrene)-modified asphalt were conducted in bonding with aggregate plates. Meanwhile, contrasting groups adopting metal plates followed the same experimental procedures. The results indicate that the influence of aggregate type on binder's rheological characteristics is dependent on the experimental variables, and microscopic characteristics and component differences should be taken into consideration when selecting aggregates in designing asphalt mixtures.

Rheological Characterization of Asphalt Fine Aggregate Matrix Using Dynamic Shear Rheometer.

Asphalt fine aggregate matrix (FAM) is a predominant component directly related to field performances of hot asphalt mix (HMA), it is necessary to investigate material properties of FAM. Prior to preparing FAM specimens, the asphalt content was calculated by keeping the filler-bitumen (FB) ratio the same as in the corresponding HMA. A non-destructive fabrication method instead of coring and cutting methods was developed to compact FAM cylinders, and the joint base was designed to be concentric with the loading axis of testing system. Rheological responses of FAM were studied using the dynamic shear rheometer (DSR). Two repeated tests prove that the FAM compactor and the jointed base meet the requirement of data validation. Results show that rheological performances of FAM are significantly affected by asphalt content, gradation, air void content, and testing frequency. Air void is concluded to be the decisive factor which influences the stability of FAM, and the fiber is demonstrated to play a role on enhancing the flow resistance of FAM-F even though with the richest asphalt content.

Impact of Ultraviolet Radiation on the Aging Properties of SBS-Modified Asphalt Binders.

Styrene Butadiene Styrene (SBS) polymer-modified asphalt binders have become widely used in asphalt pavement because of their advantages in high- and low-temperature performance and fatigue resistance. Asphalt pavement is inevitably exposed to sunlight and ultraviolet (UV) radiation during its construction and service life. However, consideration of the aging effect of UV radiation is still limited in current pavement design and evaluation systems. In order to evaluate the impact of UV radiation on the aging properties of SBS-modified asphalt binders, UV aging tests were performed on Rolling Thin Film Oven Test (RTFOT)-aged samples with different UV radiation intensities and aging times. Sixteen different groups of tests were conducted to compare the rheological properties and functional group characteristics of SBS-modified asphalt binders. Dynamic Shear Rheometer (DSR), Bending Beam Rheometer (BBR), FTIR, and SEM tests were conducted to evaluate the aging mechanisms in various UV aging conditions. The results found that UV radiation seriously destroys the network structure formed by the cross-linking effect in SBS-modified asphalt binders, which aggravates the degradation of SBS and results in a great change of rheological properties after UV aging. The nature of SBS-modified asphalt binder aging resulted from the degradation of SBS and the changes of asphalt binder base composition, which lead to the transformation of colloidal structure and the deterioration of asphalt binder performance. The tests also found that continuous UV radiation can increase shrinkage stress in the asphalt binder surface and leads to surface cracking of the asphalt binder.

Real-Time Flow Behavior of Hot Mix Asphalt (HMA) Compaction Based on Rheological Constitutive Theory.

Compaction is the most critical stage during pavement construction, but the real-time rheological behavior in the compaction process of hot mix asphalt has not received enough attention. Rheological properties directly reflect the of mixture performance, the intrinsic directly reflects the influencing factors of compaction, and the pavement compactness and service life. Therefore, it is important to interpret the rheological properties of the asphalt mixture during the compaction process. In this paper, the improved Nishihara model was used to study the viscoelastic-plastic properties of the hot mix asphalt in the compaction process. Firstly, the improved Nishihara model was briefly introduced. Subsequently, the stress and strain correlation curves are obtained by the MTS (Material Testing System) compaction test, and the strain-time curve is fitted to determine the model parameter values. Finally, the parameters are substituted into the constitutive equation to obtain the strain-time curve and compared it with the test curve. The results show that the improved Nishihara model effectively depicts the real time behavior of the asphalt mixture in the compaction progress. The viscos and plastic parameters present certain differences, which reflects that the gradation and temperature have certain influence on the compaction characteristics of the mixture.

Interlaminar Bonding Properties on Cement Concrete Deck and Phosphorous Slag Asphalt Pavement.

The slippage damage caused by weak interlaminar bonding between cement concrete deck and asphalt surface is a serious issue for bridge pavement. In order to evaluate the interlaminar bonding of cement concrete bridge deck and phosphorous slag (PS) asphalt pavement, the shear resistance properties of the bonding layer structure were studied through direct shear tests. The impact of PS as a substitute of asphalt mixture aggregate, interface characteristics, normal pressure, waterproof and cohesive layer types, temperature and shear rate on the interlaminar bonding properties were analyzed. The test results indicated that the interlaminar bonding of bridge deck pavement is improved after asphalt mixture fine aggregate was substituted with PS and PS powder, and the result indicated that the shear strength of grooved and aggregate-exposed interfaces is significantly higher than untreated interface, the PS micro-powder or anti-stripping agent can also improve the adhesion between layers when mixed into SBS asphalt. This study provided important theoretical and practical guidance for improving the shear stability of bridge deck pavement.