Evaluation of bond strength of dual resin cements to CAD/CAM-created lithium disilicate ceramic.

BACKGROUND: The objective was to examine the microshear bond strength values of different dual resin cements to computer-aided design (CAD)/computer-aided manufacturing (CAM)-created ceramics containing lithium disilicate, which underwent different surface treatments. METHODS: Two dual resin cements (RelyX ARC and RelyX Ultimate) and three surface treatments of lithium disilicate ceramic blocks (Ceramic Primer (CP; containing silane) plus Adper Scotchbond Multipurpose (ASM) adhesive; CP plus Single Bond Universal (SBU) adhesive; and SBU adhesive alone) were tested. The SBU adhesive includes silane in its formulation. Each sample underwent a microshear test and bond strength values were subjected to analysis of variance (ANOVA) followed by Tukey's test (α=0.05). Fracture patterns were also observed with light microscopy. RESULTS: RelyX ARC treated with CP+ASM or CP+SBU presented resistance values that were significantly higher than the same treatments for RelyX Ultimate. Conversely, for the blocks treated with SBU alone, the mean resistance value for RelyX Ultimate was higher than that of RelyX ARC. Regarding the different types of treatment for each resin, the mean resistance value of RelyX ARC treated with CP+ASM was significantly highest, followed by treatment with CP+SBU and SBU treatment alone. Meanwhile, RelyX Ultimate treated with CP+ASM or CP+SBU presented resistance values that were significantly higher than SBU treatment alone. In all of the groups, an adhesive fracture pattern was predominantly observed. CONCLUSIONS: The present results indicate that silanization is important for ASM and SBU adhesives to be effective.

Effects of Polymerization Mode and Interaction with Hydroxyapatite on the Rate of pH Neutralization, Mechanical Properties, and Depth of Cure in Self-Adhesive Cements.

OBJECTIVE: The aim of the study was to evaluate the physicochemical properties of self-adhesive resin cements associated with hydroxyapatite (HAp) according to the polymerization activation. MATERIALS AND METHODS: Specimens of cements (PermaCem 2.0 [DMG]; MaxCem Elite [Kerr], and RelyX U200 [3M ESPE]) were distributed into three groups: activation mode; self-cured and dual-cured modes; and association or not with HAp powder mode. The pH neutralization was evaluated as a function of time. Flexural strength and elastic modulus were also tested (0.5 mm/min.). The depth of cure was also analyzed using the scraping test (ISO 4049). Infrared spectroscopy was also used to collect the spectra of specimens to evaluate the chemical bonds. Statistical comparisons were conducted at 5% of significance. RESULTS: The aggressiveness of the self-adhesive resin cements evaluated varied among the materials with a tendency for neutralization. Self-cure groups exhibited lower pH throughout the entire evaluation when compared with that of the dual-cure ones, irrespective of the addition of HAp. MaxCem Elite when photoactivated was the only cement influenced by the addition of the HAp in terms of mechanical properties. The self-adhesive cements tested presented equivalent depth of cure based on the ISO 4049 requirements, regardless of the evaluated factors. CONCLUSIONS: Based on the parameters evaluated, the results demonstrated that most of the self-adhesive cements remained unaltered or improved when mixed with HAp, regardless of the activation mode.