Combined Spatially Resolved Characterization of Antireflection and Antisoiling Coatings for PV Module Glass.

Characterization of photovoltaic (PV) module materials throughout different stages of service life is crucial to understanding and improving the durability of these materials. Currently the large-scale of PV modules (>1 m2) is imbalanced with the small-scale of most materials characterization tools (≤1 cm2). Furthermore, understanding degradation mechanisms often requires a combination of multiple characterization techniques. Here, we present adaptations of three standard materials characterization techniques to enable mapping characterization over moderate sample areas (≥25 cm2). Contact angle, ellipsometry, and UV-vis spectroscopy are each adapted and demonstrated on two representative samples: a commercial multifunctional coating for PV glass and an oxide combinatorial sample library. Best practices are discussed for adapting characterization techniques for large-area mapping and combining mapping information from multiple techniques.

Molecular dynamics simulation of zirconium tungstate amorphization and the amorphous-crystalline interface.

Classical molecular dynamics (MD) simulations were performed to provide a conceptual understanding of the amorphous-crystalline interface for a candidate negative thermal expansion (NTE) material, ZrW2O8. Simulations of pressure-induced amorphization at 300 K indicate that an amorphous phase forms at pressures of 10 GPa and greater, and this phase persists when the pressure is subsequently decreased to 1 bar. However, the crystalline phase is recovered when the slightly distorted 5 GPa phase is relaxed to 1 bar. Simulations were also performed on a two-phase model consisting of the high-pressure amorphous phase in direct contact with the crystalline phase. Upon equilibration at 300 K and 1 bar, the crystalline phase remains unchanged beyond a thin layer of disrupted structure at the crystalline-amorphous interface. Differences in local atomic structure at the interface are quantified from the simulation trajectories.

First-Principles Structural, Mechanical, and Thermodynamic Calculations of the Negative Thermal Expansion Compound Zr2(WO4)(PO4)2.

The negative thermal expansion (NTE) material Zr2(WO4)(PO4)2 has been investigated for the first time within the framework of the density functional perturbation theory (DFPT). The structural, mechanical, and thermodynamic properties of this material have been predicted using the Perdew, Burke and Ernzerhof for solid (PBEsol) exchange-correlation functional, which showed superior accuracy over standard functionals in previous computational studies of the NTE material α-ZrW2O8. The bulk modulus calculated for Zr2(WO4)(PO4)2 using the Vinet equation of state at room temperature is K 0 = 63.6 GPa, which is in close agreement with the experimental estimate of 61.3(8) at T = 296 K. The computed mean linear coefficient of thermal expansion is -3.1 × 10-6 K-1 in the temperature range ∼0-70 K, in line with the X-ray diffraction measurements. The mean Grüneisen parameter controlling the thermal expansion of Zr2(WO4)(PO4)2 is negative below 205 K, with a minimum of -2.1 at 10 K. The calculated standard molar heat capacity and entropy are C P 0 = 287.6 and S 0 = 321.9 J·mol-1·K-1, respectively. The results reported in this study demonstrate the accuracy of DFPT/PBEsol for assessing or predicting the relationship between structural and thermomechanical properties of NTE materials.

The proteomics of senescence in leaves of white clover, Trifolium repens (L.).

A proteomics approach has been used to study changes in protein abundance during leaf senescence in white clover. Changes in cell ultrastructure were also examined using transmission electron microscopy. The most obvious ultrastructural changes during senescence occurred in chloroplasts, with progressive loss of thylakoid integrity and accumulation of osmiophilic globules in the stroma. Quantitative analysis of 590 leaf protein spots separated by two-dimensional electrophoresis indicated that approximately 40% of the spots showed significant senescence related changes in abundance. Approximately one-third of the protein spots present in mature green leaves were also visible by two-dimensional electrophoresis of an isolated chloroplast fraction, and these spots represented a major proportion of the proteins showing senescence related declines in abundance. Chloroplast proteins that were identified by matrix-assisted laser desorption/ionization-time of flight mass fingerprinting included rubisco large and small subunits, a rubisco activase and the 33 kDa protein of the photosystem II oxygen-evolving complex. These proteins declined in abundance late in senescence, indicating that the photosynthetic apparatus was being degraded. A chloroplast glutamine synthetase showed partial decline in abundance during late senescence but was maintained at levels that may support provision of glutamine for export to other tissues. The results emphasise the importance of proteolysis, chloroplast degradation and remobilisation of nitrogen in leaf senescence.