Identification of the nitrogen split interstitial (N-N)(N) in GaN.

Combining electron paramagnetic resonance, density functional theory, and positron annihilation spectroscopy (PAS), we identify the nitrogen interstitial defect in GaN. The isolated interstitial is unstable and transforms into a split interstitial configuration (N-N)(N). It is generated by particle irradiation with an introduction rate of a primary defect, pins the Fermi level at E(C)-1.0 eV for high fluences, and anneals out at 400 °C. The associated defect, the nitrogen vacancy, is observed by PAS only in the initial stage of irradiation.

High-field optically detected EPR and ENDOR of semiconductor defects using W-band microwave Fabry-Pérot resonators.

The designs of W-band (approximately 95 GHz) Fabry-Pérot microwave resonators for optically detected EPR and ENDOR using the magnetic circular dichroism of the optical absorption (MCDA) as well as for photo-luminescence-detected EPR are briefly described. We report on the first MCDA-detected high-field EPR/ENDOR investigation of the paramagnetic EL2+ defect in semi-insulating GaAs. The higher-order effects, which prevented the unambiguous analysis of previous MCDA-detected K-band EPR/ENDOR experiments could be suppressed in W-band. The analysis of the ENDOR spectra showed that an extremely precise alignment of the samples is necessary. The paramagnetic El2+ defect turned out to be an As antisite defect, which has four almost equivalent nearest 75As neighbours differing less than 1.5% in the superhyperfine interactions suggestive of an isolated As antisite, while the third 75As shell (fifth neighbour shell) is clearly of lower symmetry than expected for an isolated As antisite. We discuss as a possible solution to this paradoxical situation that EL2+ is an isolated antisite at room temperature, which at low temperature, where all magnetic resonance experiments are performed, associates itself with shallow acceptors such as Zn(Ga)- more than two nearest neighbour distances away. According to recent theoretical calculations, such 'loose' complexes with binding energies between 0.01 eV and 0.05 eV and disturb the equivalence of the nearest neighbour superhyperfine (shf) interactions less than 1.5%. Also, W-band EPR was measured using the photo-luminescence for detection to investigate P dopants in 6H-SiC.