RESUMO
We study by scanning thermal microscopy the nanoscale thermal conductance of films (40-400 nm thick) of [1]benzothieno[3,2-b][1]benzothiophene (BTBT) and 2,7-dioctyl[1]benzothieno[3,2-b][1]benzothiophene (C8-BTBT-C8). We demonstrate that the out-of-plane thermal conductivity is significant along the interlayer direction, larger for BTBT (0.63 ± 0.12 W m-1 K-1) compared to C8-BTBT-C8 (0.25 ± 0.13 W m-1 K-1). These results are supported by molecular dynamics calculations (approach to equilibrium molecular dynamics method) performed on the corresponding molecular crystals. The calculations point to significant thermal conductivity (3D-like) values along the 3 crystalline directions, with anisotropy factors between the crystalline directions below 1.8 for BTBT and below 2.8 for C8-BTBT-C8, in deep contrast with the charge transport properties featuring a two-dimensional character for these materials. In agreement with the experiments, the calculations yield larger values in BTBT compared to C8-BTBT-C8 (0.6-1.3 W m-1 K-1versus 0.3-0.7 W m-1 K-1, respectively). The weak thickness dependence of the nanoscale thermal resistance is in agreement with a simple analytical model.
RESUMO
All-polymeric flexible transparent heaters (THs) are demonstrated for the first time. Thin films of four poly(3,4-ethylenedioxythiophene) (PEDOT)-based materials embedding different dopants exhibit low sheet resistances, down to 57 Ω sq-1 associated with good transparencies (>87%) and a haze lower than 1%. These transparent thin films show excellent heating properties, with high heating rates (up to 1.6 °C s-1) and steady-state temperatures exceeding 100 °C when subjected to 12 V bias. Very high areal power densities were also measured, reaching almost 10 000 W m-2. The temperature increase is finely fitted to a thermal model. It is further demonstrated that these new THs can be efficiently integrated for applications in thermochromic displays and visor deicers.