Further Development of Polyepichlorohydrin Based Anion Exchange Membranes for Reverse Electrodialysis by Tuning Cast Solution Properties.

Recently, there have been several studies done regarding anion exchange membranes (AEMs) based on polyepichlorohydrin (PECH), an attractive polymer enabling safe membrane fabrication due to its inherent chloromethyl groups. However, there are still undiscovered properties of these membranes emerging from different compositions of cast solutions. Thus, it is vital to explore new membrane properties for sustainable energy generation by reverse electrodialysis (RED). In this study, the cast solution composition was easily tuned by varying the ratio of active polymer (i.e., blend ratio) and quaternary agent (i.e., excess diamine ratio) in the range of 1.07-2.00, and 1.00-4.00, respectively. The membrane synthesized with excess diamine ratio of 4.00 and blend ratio of 1.07 provided the best results in terms of ion exchange capacity, 3.47 mmol/g, with satisfactory conductive properties (area resistance: 2.4 Ω·cm2, electrical conductivity: 6.44 mS/cm) and high hydrophilicity. RED tests were performed by AEMs coupled with the commercially available Neosepta CMX cation exchange membrane (CEMs).

Effect of Co-Existing Ions on Salinity Gradient Power Generation by Reverse Electrodialysis Using Different Ion Exchange Membrane Pairs.

This study investigates the influence of co-existing ions on the salinity gradient power generation performance of the reverse electrodialysis (RED) using three different commercial ion exchange membrane pairs. The feed solutions, including the mixture of two different salts, were prepared with 90 wt.% of NaCl and 10 wt.% of LiCl, KCl, CaCl2, MgCl2 or Na2SO4 by keeping the salt ratio between high concentrate solution and low concentrate solution constant as 1:30 (g/g) at various flow velocities (50, 125 and 200 mL/min). It was observed that the divalent ions exhibited a negative impact on the performance of the RED system due to their high valence and low ionic mobility depending on their high hydrated radius and low diffusion coefficients compared to those of the monovalent ions. On the other hand, the effect of the monovalent ions differed according to the properties of ion exchange membranes used in the RED stack. When the power generation performances of ion exchange membrane pairs employed in the RED stack were compared, it was considered that Neosepta AMX and CMX membranes provided the highest power density due to their low membrane thicknesses, low electrical resistances, and relatively high ion exchange capacities compared to other two commercial ion exchange membrane pairs.

Comparison of Physicochemical Properties of Two Types of Polyepichlorohydrin-Based Anion Exchange Membranes for Reverse Electrodialysis.

The development of the most effective, suitable and economic ion-exchange membranes is crucial for reverse electrodialysis (RED)-the most widely studied process to harvest salinity gradient energy from mixing seawater and river water. RED utilizes two types of membranes as core elements, namely cation exchange membranes (CEM) and anion exchange membranes (AEM). Since the preparation of AEMs is more complex compared to CEMs, the design and development of anion exchange membranes have been the focus in this study. Homogeneous AEMs based on two types of polyepichlorohydrin (PECH) with different chlorine amounts (PECH-H, 37 wt% and PECH-C, 25 wt%) were synthesized, and first-time benchmarking of the membrane properties was conducted. In addition to physicochemical membrane properties, some instrumental analyses such as SEM, FTIR and DSC were investigated to characterize these anion-exchange membranes. Based on the results, although the PECH-H-type membrane had enhanced ion-exchange properties, PECH-C-based anion-exchange membranes exhibited a higher power density of 0.316 W/m2 in a lab-scale RED system. Evidently, there is room for the development of new types of PECH-C-based AEMs with great potential for energy generation in the RED process.

Tailor-made anion-exchange membranes for salinity gradient power generation using reverse electrodialysis.

Reverse electrodialysis (RED) or blue energy is a non-polluting, sustainable technology for generating power from the mixing of solutions with different salinity, that is, seawater and river water. A concentrated salt solution (e.g., seawater) and a diluted salt solution (e.g., river water) are brought into contact through an alternating series of polymeric anion-exchange membranes (AEMs) and cation-exchange membranes (CEMs), which are either selective for anions or cations. Currently available ion-exchange membranes are not optimized for RED, whereas successful RED operation notably depends on the used ion-exchange membranes. We designed such ion-exchange membranes and for the first time we show the performance of tailor-made membranes in RED. More specifically, we focus on the development of AEMs because these are much more complex to prepare. Herein we propose a safe and more environmentally friendly method and use halogenated polyethers, such as polyepichlorohydrin (PECH) as the starting material. A tertiary diamine (1,4-diazabicyclo[2.2.2]octane, DABCO) was used to introduce the ion-exchange groups by amination and for simultaneous cross-linking of the polymer membrane. Area resistances of the series of membranes ranged from 0.82 to 2.05â€…Ω cm² and permselectivities from 87 to 90 %. For the first time we showed that tailor-made ion-exchange membranes can be applied in RED. Depending on the properties and especially membrane thickness, application of these membranes in RED resulted in a high power density of 1.27 W m⁻², which exceeds the power output obtained with the commercially available AMX membranes. This shows the potential of the design of ion-exchange membranes for a viable blue energy process.

Effect of temperature on seawater desalination-water quality analyses for desalinated seawater for its use as drinking and irrigation water.

The effect of feed seawater temperature on the quality of product water in a reverse osmosis process was investigated using typical seawater at Urla Bay, Izmir region, Turkey. The tests were carried out at different feed seawater temperatures (11-23 degrees C) using two RO modules with one membrane element each. A number of variables, including pH, conductivity, total dissolved solids, salinity, rejection percentage of a number of ions (Na+, K+, Ca2+, Mg2+, Cl(-), HCO3(-), and SO4(2-)), and the levels of boron and turbidities in collected permeates, were measured. The suitability of these permeates as irrigation and drinking water was checked by comparison with water quality standards.