RESUMO
The collagen-mimetic peptide GFOGER possesses the chondrogenic potential and has been used as a cell adhesion peptide or chondrogenic inducer. Here, we prepared an injectable in situ forming composite hydrogel system comprising methoxy polyethylene glycol-b-polycaprolactone (MPEG-PCL) and GFOGER-conjugated PEG-PCL (GFOGER-PEG-PCL) with various GFOGER concentrations based on our recently patented technology. The conjugation of GFOGER to PEG-PCL was confirmed by 1H NMR, and the particle size distribution and rheological properties for the sol-gel transition behavior of the samples with respect to the GFOGER content were evaluated systemically. In vitro experiments using rat bone marrow-derived mesenchymal stem cells (BMSCs) revealed that the GFOGER-PEG-PCL hydrogel significantly enhanced expression of integrins (ß1, α2, and α11), increased expression of FAK, and induced downstream signaling of ERK and p38. Overexpression of chondrogenic markers suggested that BMSCs have the potential to differentiate into chondrogenic lineages within GFOGER-PEG-PCL samples. In vivo studies using a rat osteochondral defect model revealed that transplanted BMSCs with GFOGER0.8-PEG-PCL survived at the defect with strong chondrogenic expression after 4 weeks. The stem cell-laden GFOGER0.8-PEG-PCL hydrogel produced remarkable osteochondral regeneration at 8 weeks of transplantation, as determined by histological findings and micro-CT analysis. The histomorphological score in the GFOGER0.8-PEG-PCL + BMSCs group was ~1.7-, 2.6-, and 5.3-fold higher than that in the GFOGER0.8-PEG-PCL, MPEG-PCL, and defect groups, respectively. Taken together, these results provide an important platform for further advanced GFOGER-based stem cell research for osteochondral repair.
RESUMO
BACKGROUND: Although the use of cardiac patches is still controversial, cardiac patch has the significance in the field of the tissue engineered cardiac regeneration because it overcomes several shortcomings of intra-myocardial injection by providing a template for cells to form a cohesive sheet. So far, fibrous scaffolds fabricated using electrospinning technique have been increasingly explored for preparation of cardiac patches. One of the problems with the use of electrospinning is that nanofibrous structures hardly allow the infiltration of cells for development of 3D tissue construct. In this respect, we have prepared novel bi-modal electrospun scaffolds as a feasible strategy to address the challenges in cardiac tissue engineering . METHODS: Nano/micro bimodal composite fibrous patch composed of collagen and poly (D, L-lactic-co-glycolic acid) (Col/PLGA) was fabricated using an independent nozzle control multi-electrospinning apparatus, and its feasibility as the stem cell laden cardiac patch was systemically investigated. RESULTS: Nano/micro bimodal distributions of Col/PLGA patches without beaded fibers were obtained in the range of the 4-6% collagen concentration. The poor mechanical properties of collagen and the hydrophobic property of PLGA were improved by co-electrospinning. In vitro experiments using bone marrow-derived mesenchymal stem cells (BMSCs) revealed that Col/PLGA showed improved cyto-compatibility and proliferation capacity compared to PLGA, and their extent increased with increase in collagen content. The results of tracing nanoparticle-labeled as well as GFP transfected BMSCs strongly support that Col/PLGA possesses the long-term stem cells retention capability, thereby allowing stem cells to directly function as myocardial and vascular endothelial cells or to secrete the recovery factors, which in turn leads to improved heart function proved by histological and echocardiographic findings. CONCLUSION: Col/PLGA bimodal cardiac patch could significantly attenuate cardiac remodeling and fully recover the cardiac function, as a consequence of their potent long term stem cell engraftment capability.
RESUMO
Although chitosan is the second most abundant natural polymer on earth, with a wide range of biomaterial applications, its poor water solubility limits general printing process. We selected water-soluble methacrylated glycol chitosan (MeGC) as an alternative and prepared a MeGC-based MG-63 cell-laden bioink for 3D printing using a visible light curing system. Optimal cell-laden 3D printing of MeGC was completed at 3% using 12 µM of riboflavin as a photoinitiator under an irradiation for 70 s, a 26-gauge nozzle, a pneumatic pressure of 120 kPa, and a printing speed of 6 mm/s, as confirmed by printability, protein adsorption, cell viability, cell proliferation, and osteogenic capability. In addition, in vitro tests showed that MeGC-70 has a viability above 92%, a proliferation above 96%, and a hemolysis level below 2%. The results demonstrate the potential for MeGC-70 bioinks and 3D printed scaffolds to be used as patient-specific scaffolds for bone regeneration purposes.